ACI-ASTM CH20 Steel vs. ACI-ASTM CK35MN Steel

Both ACI-ASTM CH20 steel and ACI-ASTM CK35MN steel are iron alloys. Both are furnished in the heat treated (HT) condition. They have 86% of their average alloy composition in common.

For each property being compared, the top bar is ACI-ASTM CH20 steel and the bottom bar is ACI-ASTM CK35MN steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
190
Elastic (Young's, Tensile) Modulus, GPa 200
210
Elongation at Break, % 38
40
Fatigue Strength, MPa 290
270
Poisson's Ratio 0.27
0.28
Shear Modulus, GPa 78
81
Tensile Strength: Ultimate (UTS), MPa 610
650
Tensile Strength: Yield (Proof), MPa 350
310

Thermal Properties

Latent Heat of Fusion, J/g 310
310
Maximum Temperature: Corrosion, °C 440
440
Maximum Temperature: Mechanical, °C 1100
1100
Melting Completion (Liquidus), °C 1410
1460
Melting Onset (Solidus), °C 1430
1410
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 14
12
Thermal Expansion, µm/m-K 15
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
1.9
Electrical Conductivity: Equal Weight (Specific), % IACS 2.3
2.1

Otherwise Unclassified Properties

Base Metal Price, % relative 20
31
Density, g/cm3 7.8
8.0
Embodied Carbon, kg CO2/kg material 3.7
5.9
Embodied Energy, MJ/kg 53
81
Embodied Water, L/kg 180
210

Common Calculations

PREN (Pitting Resistance) 25
48
Resilience: Ultimate (Unit Rupture Work), MJ/m3 200
210
Resilience: Unit (Modulus of Resilience), kJ/m3 300
240
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 22
22
Strength to Weight: Bending, points 21
21
Thermal Diffusivity, mm2/s 3.7
3.3
Thermal Shock Resistance, points 15
14

Alloy Composition

Carbon (C), % 0 to 0.2
0 to 0.035
Chromium (Cr), % 22 to 26
22 to 24
Copper (Cu), % 0
0 to 0.4
Iron (Fe), % 54.7 to 66
43.4 to 51.8
Manganese (Mn), % 0 to 1.5
0 to 2.0
Molybdenum (Mo), % 0 to 0.5
6.0 to 6.8
Nickel (Ni), % 12 to 15
20 to 22
Nitrogen (N), % 0
0.21 to 0.32
Phosphorus (P), % 0 to 0.040
0 to 0.035
Silicon (Si), % 0 to 2.0
0 to 1.0
Sulfur (S), % 0 to 0.040
0 to 0.020