ACI-ASTM CH20 Steel vs. ACI-ASTM CT15C Steel

Both ACI-ASTM CH20 steel and ACI-ASTM CT15C steel are iron alloys. They have 80% of their average alloy composition in common.

For each property being compared, the top bar is ACI-ASTM CH20 steel and the bottom bar is ACI-ASTM CT15C steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
140
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 38
23
Fatigue Strength, MPa 290
130
Poisson's Ratio 0.27
0.28
Shear Modulus, GPa 78
76
Tensile Strength: Ultimate (UTS), MPa 610
500
Tensile Strength: Yield (Proof), MPa 350
190

Thermal Properties

Latent Heat of Fusion, J/g 310
310
Maximum Temperature: Corrosion, °C 440
560
Maximum Temperature: Mechanical, °C 1100
1080
Melting Completion (Liquidus), °C 1410
1410
Melting Onset (Solidus), °C 1430
1360
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 14
12
Thermal Expansion, µm/m-K 15
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 2.3
1.9

Otherwise Unclassified Properties

Base Metal Price, % relative 20
36
Density, g/cm3 7.8
8.0
Embodied Carbon, kg CO2/kg material 3.7
6.1
Embodied Energy, MJ/kg 53
88
Embodied Water, L/kg 180
190

Common Calculations

PREN (Pitting Resistance) 25
20
Resilience: Ultimate (Unit Rupture Work), MJ/m3 200
90
Resilience: Unit (Modulus of Resilience), kJ/m3 300
93
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 22
17
Strength to Weight: Bending, points 21
17
Thermal Diffusivity, mm2/s 3.7
3.2
Thermal Shock Resistance, points 15
12

Alloy Composition

Carbon (C), % 0 to 0.2
0.050 to 0.15
Chromium (Cr), % 22 to 26
19 to 21
Iron (Fe), % 54.7 to 66
40.3 to 49.2
Manganese (Mn), % 0 to 1.5
0.15 to 1.5
Molybdenum (Mo), % 0 to 0.5
0
Nickel (Ni), % 12 to 15
31 to 34
Niobium (Nb), % 0
0.5 to 1.5
Phosphorus (P), % 0 to 0.040
0 to 0.030
Silicon (Si), % 0 to 2.0
0.15 to 1.5
Sulfur (S), % 0 to 0.040
0 to 0.030