ACI-ASTM CH20 Steel vs. EN 1.4035 Stainless Steel

Both ACI-ASTM CH20 steel and EN 1.4035 stainless steel are iron alloys. They have 75% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CH20 steel and the bottom bar is EN 1.4035 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
220
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 38
18
Fatigue Strength, MPa 290
250
Poisson's Ratio 0.27
0.28
Shear Modulus, GPa 78
76
Tensile Strength: Ultimate (UTS), MPa 610
690
Tensile Strength: Yield (Proof), MPa 350
400

Thermal Properties

Latent Heat of Fusion, J/g 310
270
Maximum Temperature: Corrosion, °C 440
380
Maximum Temperature: Mechanical, °C 1100
760
Melting Completion (Liquidus), °C 1410
1430
Melting Onset (Solidus), °C 1430
1390
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 14
29
Thermal Expansion, µm/m-K 15
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
3.0
Electrical Conductivity: Equal Weight (Specific), % IACS 2.3
3.5

Otherwise Unclassified Properties

Base Metal Price, % relative 20
7.0
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 3.7
2.0
Embodied Energy, MJ/kg 53
27
Embodied Water, L/kg 180
100

Common Calculations

PREN (Pitting Resistance) 25
13
Resilience: Ultimate (Unit Rupture Work), MJ/m3 200
110
Resilience: Unit (Modulus of Resilience), kJ/m3 300
420
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 22
25
Strength to Weight: Bending, points 21
22
Thermal Diffusivity, mm2/s 3.7
7.8
Thermal Shock Resistance, points 15
25

Alloy Composition

Carbon (C), % 0 to 0.2
0.43 to 0.5
Chromium (Cr), % 22 to 26
12.5 to 14
Iron (Fe), % 54.7 to 66
82.1 to 86.9
Manganese (Mn), % 0 to 1.5
0 to 2.0
Molybdenum (Mo), % 0 to 0.5
0
Nickel (Ni), % 12 to 15
0
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 2.0
0 to 1.0
Sulfur (S), % 0 to 0.040
0.15 to 0.35