ACI-ASTM CH20 Steel vs. EN 1.4446 Stainless Steel

Both ACI-ASTM CH20 steel and EN 1.4446 stainless steel are iron alloys. They have a moderately high 93% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CH20 steel and the bottom bar is EN 1.4446 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
140
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 38
23
Fatigue Strength, MPa 290
160
Poisson's Ratio 0.27
0.28
Shear Modulus, GPa 78
79
Tensile Strength: Ultimate (UTS), MPa 610
490
Tensile Strength: Yield (Proof), MPa 350
240

Thermal Properties

Latent Heat of Fusion, J/g 310
290
Maximum Temperature: Corrosion, °C 440
410
Maximum Temperature: Mechanical, °C 1100
980
Melting Completion (Liquidus), °C 1410
1460
Melting Onset (Solidus), °C 1430
1410
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 14
14
Thermal Expansion, µm/m-K 15
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 2.3
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 20
22
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 3.7
4.5
Embodied Energy, MJ/kg 53
60
Embodied Water, L/kg 180
160

Common Calculations

PREN (Pitting Resistance) 25
34
Resilience: Ultimate (Unit Rupture Work), MJ/m3 200
93
Resilience: Unit (Modulus of Resilience), kJ/m3 300
140
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 22
17
Strength to Weight: Bending, points 21
17
Thermal Diffusivity, mm2/s 3.7
3.6
Thermal Shock Resistance, points 15
11

Alloy Composition

Carbon (C), % 0 to 0.2
0 to 0.030
Chromium (Cr), % 22 to 26
16.5 to 18.5
Iron (Fe), % 54.7 to 66
59.7 to 66.9
Manganese (Mn), % 0 to 1.5
0 to 1.5
Molybdenum (Mo), % 0 to 0.5
4.0 to 4.5
Nickel (Ni), % 12 to 15
12.5 to 14.5
Nitrogen (N), % 0
0.12 to 0.22
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 2.0
0 to 1.0
Sulfur (S), % 0 to 0.040
0 to 0.030