ACI-ASTM CH20 Steel vs. EN 1.4525 Stainless Steel

Both ACI-ASTM CH20 steel and EN 1.4525 stainless steel are iron alloys. They have 82% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CH20 steel and the bottom bar is EN 1.4525 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 38
5.6 to 13
Fatigue Strength, MPa 290
480 to 540
Poisson's Ratio 0.27
0.28
Shear Modulus, GPa 78
76
Tensile Strength: Ultimate (UTS), MPa 610
1030 to 1250
Tensile Strength: Yield (Proof), MPa 350
840 to 1120

Thermal Properties

Latent Heat of Fusion, J/g 310
280
Maximum Temperature: Corrosion, °C 440
430
Maximum Temperature: Mechanical, °C 1100
860
Melting Completion (Liquidus), °C 1410
1430
Melting Onset (Solidus), °C 1430
1390
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 14
18
Thermal Expansion, µm/m-K 15
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 2.3
2.6

Otherwise Unclassified Properties

Base Metal Price, % relative 20
13
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 3.7
2.8
Embodied Energy, MJ/kg 53
39
Embodied Water, L/kg 180
130

Common Calculations

PREN (Pitting Resistance) 25
18
Resilience: Ultimate (Unit Rupture Work), MJ/m3 200
68 to 130
Resilience: Unit (Modulus of Resilience), kJ/m3 300
1820 to 3230
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 22
36 to 45
Strength to Weight: Bending, points 21
29 to 33
Thermal Diffusivity, mm2/s 3.7
4.7
Thermal Shock Resistance, points 15
34 to 41

Alloy Composition

Carbon (C), % 0 to 0.2
0 to 0.070
Chromium (Cr), % 22 to 26
15 to 17
Copper (Cu), % 0
2.5 to 4.0
Iron (Fe), % 54.7 to 66
70.4 to 79
Manganese (Mn), % 0 to 1.5
0 to 1.0
Molybdenum (Mo), % 0 to 0.5
0 to 0.8
Nickel (Ni), % 12 to 15
3.5 to 5.5
Niobium (Nb), % 0
0 to 0.35
Nitrogen (N), % 0
0 to 0.050
Phosphorus (P), % 0 to 0.040
0 to 0.035
Silicon (Si), % 0 to 2.0
0 to 0.8
Sulfur (S), % 0 to 0.040
0 to 0.025