ACI-ASTM CH20 Steel vs. EN 1.4849 Stainless Steel

Both ACI-ASTM CH20 steel and EN 1.4849 stainless steel are iron alloys. They have 73% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CH20 steel and the bottom bar is EN 1.4849 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
140
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 38
4.5
Fatigue Strength, MPa 290
120
Poisson's Ratio 0.27
0.28
Shear Modulus, GPa 78
75
Tensile Strength: Ultimate (UTS), MPa 610
480
Tensile Strength: Yield (Proof), MPa 350
250

Thermal Properties

Latent Heat of Fusion, J/g 310
320
Maximum Temperature: Corrosion, °C 440
620
Maximum Temperature: Mechanical, °C 1100
1020
Melting Completion (Liquidus), °C 1410
1390
Melting Onset (Solidus), °C 1430
1340
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 14
12
Thermal Expansion, µm/m-K 15
15

Otherwise Unclassified Properties

Base Metal Price, % relative 20
42
Density, g/cm3 7.8
8.0
Embodied Carbon, kg CO2/kg material 3.7
7.1
Embodied Energy, MJ/kg 53
100
Embodied Water, L/kg 180
200

Common Calculations

PREN (Pitting Resistance) 25
20
Resilience: Ultimate (Unit Rupture Work), MJ/m3 200
18
Resilience: Unit (Modulus of Resilience), kJ/m3 300
160
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 22
17
Strength to Weight: Bending, points 21
17
Thermal Diffusivity, mm2/s 3.7
3.2
Thermal Shock Resistance, points 15
11

Alloy Composition

Carbon (C), % 0 to 0.2
0.3 to 0.5
Chromium (Cr), % 22 to 26
18 to 21
Iron (Fe), % 54.7 to 66
32.6 to 43.5
Manganese (Mn), % 0 to 1.5
0 to 2.0
Molybdenum (Mo), % 0 to 0.5
0 to 0.5
Nickel (Ni), % 12 to 15
36 to 39
Niobium (Nb), % 0
1.2 to 1.8
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 2.0
1.0 to 2.5
Sulfur (S), % 0 to 0.040
0 to 0.030