ACI-ASTM CH20 Steel vs. EN 1.4876 Stainless Steel

Both ACI-ASTM CH20 steel and EN 1.4876 stainless steel are iron alloys. They have 80% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CH20 steel and the bottom bar is EN 1.4876 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
170
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 38
33
Fatigue Strength, MPa 290
150
Poisson's Ratio 0.27
0.28
Shear Modulus, GPa 78
77
Tensile Strength: Ultimate (UTS), MPa 610
570
Tensile Strength: Yield (Proof), MPa 350
190

Thermal Properties

Latent Heat of Fusion, J/g 310
300
Maximum Temperature: Corrosion, °C 440
490
Maximum Temperature: Mechanical, °C 1100
1100
Melting Completion (Liquidus), °C 1410
1400
Melting Onset (Solidus), °C 1430
1350
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 14
12
Thermal Expansion, µm/m-K 15
14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 2.3
1.9

Otherwise Unclassified Properties

Base Metal Price, % relative 20
30
Density, g/cm3 7.8
8.0
Embodied Carbon, kg CO2/kg material 3.7
5.3
Embodied Energy, MJ/kg 53
76
Embodied Water, L/kg 180
200

Common Calculations

PREN (Pitting Resistance) 25
21
Resilience: Ultimate (Unit Rupture Work), MJ/m3 200
140
Resilience: Unit (Modulus of Resilience), kJ/m3 300
94
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 22
20
Strength to Weight: Bending, points 21
19
Thermal Diffusivity, mm2/s 3.7
3.2
Thermal Shock Resistance, points 15
14

Alloy Composition

Aluminum (Al), % 0
0.15 to 0.6
Carbon (C), % 0 to 0.2
0 to 0.12
Chromium (Cr), % 22 to 26
19 to 23
Iron (Fe), % 54.7 to 66
38.6 to 50.7
Manganese (Mn), % 0 to 1.5
0 to 2.0
Molybdenum (Mo), % 0 to 0.5
0
Nickel (Ni), % 12 to 15
30 to 34
Phosphorus (P), % 0 to 0.040
0 to 0.030
Silicon (Si), % 0 to 2.0
0 to 1.0
Sulfur (S), % 0 to 0.040
0 to 0.015
Titanium (Ti), % 0
0.15 to 0.6