ACI-ASTM CH20 Steel vs. EN 1.6982 Stainless Steel

Both ACI-ASTM CH20 steel and EN 1.6982 stainless steel are iron alloys. They have 79% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CH20 steel and the bottom bar is EN 1.6982 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 38
17
Fatigue Strength, MPa 290
350
Poisson's Ratio 0.27
0.28
Shear Modulus, GPa 78
76
Tensile Strength: Ultimate (UTS), MPa 610
800
Tensile Strength: Yield (Proof), MPa 350
570

Thermal Properties

Latent Heat of Fusion, J/g 310
280
Maximum Temperature: Corrosion, °C 440
390
Maximum Temperature: Mechanical, °C 1100
770
Melting Completion (Liquidus), °C 1410
1440
Melting Onset (Solidus), °C 1430
1400
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 14
25
Thermal Expansion, µm/m-K 15
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
2.7
Electrical Conductivity: Equal Weight (Specific), % IACS 2.3
3.2

Otherwise Unclassified Properties

Base Metal Price, % relative 20
10
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 3.7
2.4
Embodied Energy, MJ/kg 53
33
Embodied Water, L/kg 180
110

Common Calculations

PREN (Pitting Resistance) 25
14
Resilience: Ultimate (Unit Rupture Work), MJ/m3 200
120
Resilience: Unit (Modulus of Resilience), kJ/m3 300
820
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 22
28
Strength to Weight: Bending, points 21
25
Thermal Diffusivity, mm2/s 3.7
6.6
Thermal Shock Resistance, points 15
29

Alloy Composition

Carbon (C), % 0 to 0.2
0 to 0.050
Chromium (Cr), % 22 to 26
12 to 13.5
Iron (Fe), % 54.7 to 66
78.7 to 84.5
Manganese (Mn), % 0 to 1.5
0 to 1.0
Molybdenum (Mo), % 0 to 0.5
0 to 0.7
Nickel (Ni), % 12 to 15
3.5 to 5.0
Phosphorus (P), % 0 to 0.040
0 to 0.035
Silicon (Si), % 0 to 2.0
0 to 1.0
Sulfur (S), % 0 to 0.040
0 to 0.015