ACI-ASTM CH20 Steel vs. EN 1.7336 Steel

Both ACI-ASTM CH20 steel and EN 1.7336 steel are iron alloys. They have 63% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CH20 steel and the bottom bar is EN 1.7336 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
180
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 38
22
Fatigue Strength, MPa 290
240 to 310
Poisson's Ratio 0.27
0.29
Shear Modulus, GPa 78
73
Tensile Strength: Ultimate (UTS), MPa 610
590
Tensile Strength: Yield (Proof), MPa 350
340 to 440

Thermal Properties

Latent Heat of Fusion, J/g 310
260
Maximum Temperature: Mechanical, °C 1100
430
Melting Completion (Liquidus), °C 1410
1460
Melting Onset (Solidus), °C 1430
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 14
40
Thermal Expansion, µm/m-K 15
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
7.5
Electrical Conductivity: Equal Weight (Specific), % IACS 2.3
8.6

Otherwise Unclassified Properties

Base Metal Price, % relative 20
3.1
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 3.7
1.6
Embodied Energy, MJ/kg 53
21
Embodied Water, L/kg 180
53

Common Calculations

PREN (Pitting Resistance) 25
3.2
Resilience: Ultimate (Unit Rupture Work), MJ/m3 200
110 to 120
Resilience: Unit (Modulus of Resilience), kJ/m3 300
310 to 510
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 22
21
Strength to Weight: Bending, points 21
20
Thermal Diffusivity, mm2/s 3.7
11
Thermal Shock Resistance, points 15
17

Alloy Composition

Carbon (C), % 0 to 0.2
0 to 0.17
Chromium (Cr), % 22 to 26
1.0 to 1.5
Copper (Cu), % 0
0 to 0.3
Iron (Fe), % 54.7 to 66
95.6 to 97.7
Manganese (Mn), % 0 to 1.5
0.4 to 0.65
Molybdenum (Mo), % 0 to 0.5
0.45 to 0.65
Nickel (Ni), % 12 to 15
0 to 0.3
Nitrogen (N), % 0
0 to 0.012
Phosphorus (P), % 0 to 0.040
0 to 0.015
Silicon (Si), % 0 to 2.0
0.5 to 0.8
Sulfur (S), % 0 to 0.040
0 to 0.0050