ACI-ASTM CH20 Steel vs. C83300 Brass

ACI-ASTM CH20 steel belongs to the iron alloys classification, while C83300 brass belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CH20 steel and the bottom bar is C83300 brass.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
35
Elastic (Young's, Tensile) Modulus, GPa 200
110
Elongation at Break, % 38
35
Poisson's Ratio 0.27
0.34
Shear Modulus, GPa 78
42
Tensile Strength: Ultimate (UTS), MPa 610
220
Tensile Strength: Yield (Proof), MPa 350
69

Thermal Properties

Latent Heat of Fusion, J/g 310
200
Maximum Temperature: Mechanical, °C 1100
180
Melting Completion (Liquidus), °C 1410
1060
Melting Onset (Solidus), °C 1430
1030
Specific Heat Capacity, J/kg-K 480
380
Thermal Conductivity, W/m-K 14
160
Thermal Expansion, µm/m-K 15
18

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
32
Electrical Conductivity: Equal Weight (Specific), % IACS 2.3
33

Otherwise Unclassified Properties

Base Metal Price, % relative 20
30
Density, g/cm3 7.8
8.8
Embodied Carbon, kg CO2/kg material 3.7
2.7
Embodied Energy, MJ/kg 53
44
Embodied Water, L/kg 180
320

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 200
60
Resilience: Unit (Modulus of Resilience), kJ/m3 300
21
Stiffness to Weight: Axial, points 14
7.0
Stiffness to Weight: Bending, points 25
18
Strength to Weight: Axial, points 22
6.9
Strength to Weight: Bending, points 21
9.2
Thermal Diffusivity, mm2/s 3.7
48
Thermal Shock Resistance, points 15
7.9

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Carbon (C), % 0 to 0.2
0
Chromium (Cr), % 22 to 26
0
Copper (Cu), % 0
92 to 94
Iron (Fe), % 54.7 to 66
0
Lead (Pb), % 0
1.0 to 2.0
Manganese (Mn), % 0 to 1.5
0
Molybdenum (Mo), % 0 to 0.5
0
Nickel (Ni), % 12 to 15
0
Phosphorus (P), % 0 to 0.040
0
Silicon (Si), % 0 to 2.0
0
Sulfur (S), % 0 to 0.040
0
Tin (Sn), % 0
1.0 to 2.0
Zinc (Zn), % 0
2.0 to 6.0
Residuals, % 0
0 to 0.7