ACI-ASTM CK20 Steel vs. ACI-ASTM CF10SMnN Steel

Both ACI-ASTM CK20 steel and ACI-ASTM CF10SMnN steel are iron alloys. Both are furnished in the heat treated (HT) condition. They have 80% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CK20 steel and the bottom bar is ACI-ASTM CF10SMnN steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 150
190
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 37
34
Fatigue Strength, MPa 220
260
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 78
75
Tensile Strength: Ultimate (UTS), MPa 530
660
Tensile Strength: Yield (Proof), MPa 260
330

Thermal Properties

Latent Heat of Fusion, J/g 310
340
Maximum Temperature: Corrosion, °C 440
410
Maximum Temperature: Mechanical, °C 1100
900
Melting Completion (Liquidus), °C 1400
1360
Melting Onset (Solidus), °C 1430
1310
Specific Heat Capacity, J/kg-K 480
500
Thermal Expansion, µm/m-K 15
16

Otherwise Unclassified Properties

Base Metal Price, % relative 25
15
Density, g/cm3 7.8
7.5
Embodied Carbon, kg CO2/kg material 4.4
3.1
Embodied Energy, MJ/kg 62
45
Embodied Water, L/kg 190
150

Common Calculations

PREN (Pitting Resistance) 26
19
Resilience: Ultimate (Unit Rupture Work), MJ/m3 160
180
Resilience: Unit (Modulus of Resilience), kJ/m3 170
280
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
26
Strength to Weight: Axial, points 19
24
Strength to Weight: Bending, points 19
22
Thermal Shock Resistance, points 13
15

Alloy Composition

Carbon (C), % 0 to 0.2
0 to 0.1
Chromium (Cr), % 23 to 27
16 to 18
Iron (Fe), % 46.7 to 58
59.1 to 65.4
Manganese (Mn), % 0 to 2.0
7.0 to 9.0
Molybdenum (Mo), % 0 to 0.5
0
Nickel (Ni), % 19 to 22
8.0 to 9.0
Nitrogen (N), % 0
0.080 to 0.18
Phosphorus (P), % 0 to 0.040
0 to 0.060
Silicon (Si), % 0 to 2.0
3.5 to 4.5
Sulfur (S), % 0 to 0.040
0 to 0.030