ACI-ASTM CK20 Steel vs. Automotive Grey Cast Iron

Both ACI-ASTM CK20 steel and automotive grey cast iron are iron alloys. There are 28 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CK20 steel and the bottom bar is automotive grey cast iron.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 150
160 to 280
Elastic (Young's, Tensile) Modulus, GPa 200
180
Elongation at Break, % 37
9.6 to 14
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 78
69 to 70
Tensile Strength: Ultimate (UTS), MPa 530
140 to 290
Tensile Strength: Yield (Proof), MPa 260
94 to 200

Thermal Properties

Latent Heat of Fusion, J/g 310
260 to 280
Melting Completion (Liquidus), °C 1400
1380 to 1390
Melting Onset (Solidus), °C 1430
1340 to 1350
Specific Heat Capacity, J/kg-K 480
490
Thermal Conductivity, W/m-K 14
41 to 43
Thermal Expansion, µm/m-K 15
12 to 14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
7.4 to 7.6
Electrical Conductivity: Equal Weight (Specific), % IACS 2.3
8.8 to 9.1

Otherwise Unclassified Properties

Base Metal Price, % relative 25
1.9 to 3.0
Density, g/cm3 7.8
7.5 to 7.6
Embodied Carbon, kg CO2/kg material 4.4
1.5 to 1.7
Embodied Energy, MJ/kg 62
21 to 24
Embodied Water, L/kg 190
44 to 51

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 160
18 to 25
Resilience: Unit (Modulus of Resilience), kJ/m3 170
25 to 110
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 19
5.2 to 11
Strength to Weight: Bending, points 19
8.0 to 13
Thermal Diffusivity, mm2/s 3.7
11 to 12
Thermal Shock Resistance, points 13
4.2 to 8.6