ACI-ASTM CK20 Steel vs. EN 1.0143 Steel

Both ACI-ASTM CK20 steel and EN 1.0143 steel are iron alloys. They have 53% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CK20 steel and the bottom bar is EN 1.0143 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 150
140
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 37
21
Fatigue Strength, MPa 220
180
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 78
73
Tensile Strength: Ultimate (UTS), MPa 530
470
Tensile Strength: Yield (Proof), MPa 260
250

Thermal Properties

Latent Heat of Fusion, J/g 310
250
Maximum Temperature: Mechanical, °C 1100
400
Melting Completion (Liquidus), °C 1400
1460
Melting Onset (Solidus), °C 1430
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 14
51
Thermal Expansion, µm/m-K 15
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 2.3
8.2

Otherwise Unclassified Properties

Base Metal Price, % relative 25
1.9
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 4.4
1.4
Embodied Energy, MJ/kg 62
18
Embodied Water, L/kg 190
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 160
85
Resilience: Unit (Modulus of Resilience), kJ/m3 170
170
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 19
17
Strength to Weight: Bending, points 19
17
Thermal Diffusivity, mm2/s 3.7
14
Thermal Shock Resistance, points 13
15

Alloy Composition

Carbon (C), % 0 to 0.2
0 to 0.21
Chromium (Cr), % 23 to 27
0
Copper (Cu), % 0
0 to 0.6
Iron (Fe), % 46.7 to 58
97.5 to 100
Manganese (Mn), % 0 to 2.0
0 to 1.6
Molybdenum (Mo), % 0 to 0.5
0
Nickel (Ni), % 19 to 22
0
Nitrogen (N), % 0
0 to 0.014
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 2.0
0
Sulfur (S), % 0 to 0.040
0 to 0.040