ACI-ASTM CK20 Steel vs. EN 1.0488 Steel

Both ACI-ASTM CK20 steel and EN 1.0488 steel are iron alloys. They have 54% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CK20 steel and the bottom bar is EN 1.0488 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 150
130
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 37
27
Fatigue Strength, MPa 220
210
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 78
73
Tensile Strength: Ultimate (UTS), MPa 530
440
Tensile Strength: Yield (Proof), MPa 260
280

Thermal Properties

Latent Heat of Fusion, J/g 310
250
Maximum Temperature: Mechanical, °C 1100
400
Melting Completion (Liquidus), °C 1400
1460
Melting Onset (Solidus), °C 1430
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 14
49
Thermal Expansion, µm/m-K 15
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 2.3
8.4

Otherwise Unclassified Properties

Base Metal Price, % relative 25
2.3
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 4.4
1.5
Embodied Energy, MJ/kg 62
20
Embodied Water, L/kg 190
49

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 160
100
Resilience: Unit (Modulus of Resilience), kJ/m3 170
200
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 19
15
Strength to Weight: Bending, points 19
16
Thermal Diffusivity, mm2/s 3.7
13
Thermal Shock Resistance, points 13
14

Alloy Composition

Aluminum (Al), % 0
0.020 to 0.024
Carbon (C), % 0 to 0.2
0 to 0.16
Chromium (Cr), % 23 to 27
0 to 0.3
Copper (Cu), % 0
0 to 0.3
Iron (Fe), % 46.7 to 58
96.6 to 99.38
Manganese (Mn), % 0 to 2.0
0.6 to 1.5
Molybdenum (Mo), % 0 to 0.5
0 to 0.080
Nickel (Ni), % 19 to 22
0 to 0.5
Niobium (Nb), % 0
0 to 0.050
Nitrogen (N), % 0
0 to 0.012
Phosphorus (P), % 0 to 0.040
0 to 0.025
Silicon (Si), % 0 to 2.0
0 to 0.4
Sulfur (S), % 0 to 0.040
0 to 0.0080
Titanium (Ti), % 0
0 to 0.030
Vanadium (V), % 0
0 to 0.050