ACI-ASTM CK20 Steel vs. EN 1.1181 Steel

Both ACI-ASTM CK20 steel and EN 1.1181 steel are iron alloys. They have 54% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CK20 steel and the bottom bar is EN 1.1181 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 150
160 to 180
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 37
19 to 20
Fatigue Strength, MPa 220
190 to 260
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 78
73
Tensile Strength: Ultimate (UTS), MPa 530
560 to 620
Tensile Strength: Yield (Proof), MPa 260
280 to 380

Thermal Properties

Latent Heat of Fusion, J/g 310
250
Maximum Temperature: Mechanical, °C 1100
400
Melting Completion (Liquidus), °C 1400
1460
Melting Onset (Solidus), °C 1430
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 14
42
Thermal Expansion, µm/m-K 15
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 2.3
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 25
2.1
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 4.4
1.4
Embodied Energy, MJ/kg 62
19
Embodied Water, L/kg 190
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 160
90 to 110
Resilience: Unit (Modulus of Resilience), kJ/m3 170
210 to 380
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 19
20 to 22
Strength to Weight: Bending, points 19
19 to 21
Thermal Diffusivity, mm2/s 3.7
11
Thermal Shock Resistance, points 13
19 to 21

Alloy Composition

Carbon (C), % 0 to 0.2
0.32 to 0.39
Chromium (Cr), % 23 to 27
0 to 0.4
Iron (Fe), % 46.7 to 58
97.4 to 99.18
Manganese (Mn), % 0 to 2.0
0.5 to 0.8
Molybdenum (Mo), % 0 to 0.5
0 to 0.1
Nickel (Ni), % 19 to 22
0 to 0.4
Phosphorus (P), % 0 to 0.040
0 to 0.035
Silicon (Si), % 0 to 2.0
0 to 0.4
Sulfur (S), % 0 to 0.040
0 to 0.035