ACI-ASTM CK20 Steel vs. EN 1.4462 Stainless Steel

Both ACI-ASTM CK20 steel and EN 1.4462 stainless steel are iron alloys. They have 82% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CK20 steel and the bottom bar is EN 1.4462 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 150
240
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 37
26
Fatigue Strength, MPa 220
370
Poisson's Ratio 0.28
0.27
Shear Modulus, GPa 78
80
Tensile Strength: Ultimate (UTS), MPa 530
780
Tensile Strength: Yield (Proof), MPa 260
520

Thermal Properties

Latent Heat of Fusion, J/g 310
300
Maximum Temperature: Corrosion, °C 440
430
Maximum Temperature: Mechanical, °C 1100
1060
Melting Completion (Liquidus), °C 1400
1450
Melting Onset (Solidus), °C 1430
1400
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 14
15
Thermal Expansion, µm/m-K 15
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 2.3
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 25
17
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 4.4
3.6
Embodied Energy, MJ/kg 62
49
Embodied Water, L/kg 190
160

Common Calculations

PREN (Pitting Resistance) 26
34
Resilience: Ultimate (Unit Rupture Work), MJ/m3 160
180
Resilience: Unit (Modulus of Resilience), kJ/m3 170
670
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 19
28
Strength to Weight: Bending, points 19
24
Thermal Diffusivity, mm2/s 3.7
4.0
Thermal Shock Resistance, points 13
21

Alloy Composition

Carbon (C), % 0 to 0.2
0 to 0.030
Chromium (Cr), % 23 to 27
21 to 23
Iron (Fe), % 46.7 to 58
63.7 to 71.9
Manganese (Mn), % 0 to 2.0
0 to 2.0
Molybdenum (Mo), % 0 to 0.5
2.5 to 3.5
Nickel (Ni), % 19 to 22
4.5 to 6.5
Nitrogen (N), % 0
0.1 to 0.22
Phosphorus (P), % 0 to 0.040
0 to 0.035
Silicon (Si), % 0 to 2.0
0 to 1.0
Sulfur (S), % 0 to 0.040
0 to 0.015