ACI-ASTM CK20 Steel vs. EN 1.4919 Stainless Steel

Both ACI-ASTM CK20 steel and EN 1.4919 stainless steel are iron alloys. They have 83% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CK20 steel and the bottom bar is EN 1.4919 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 150
180
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 37
40
Fatigue Strength, MPa 220
200
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 78
78
Tensile Strength: Ultimate (UTS), MPa 530
590
Tensile Strength: Yield (Proof), MPa 260
230

Thermal Properties

Latent Heat of Fusion, J/g 310
290
Maximum Temperature: Corrosion, °C 440
410
Maximum Temperature: Mechanical, °C 1100
950
Melting Completion (Liquidus), °C 1400
1440
Melting Onset (Solidus), °C 1430
1400
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 14
16
Thermal Expansion, µm/m-K 15
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
2.3
Electrical Conductivity: Equal Weight (Specific), % IACS 2.3
2.7

Otherwise Unclassified Properties

Base Metal Price, % relative 25
19
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 4.4
3.8
Embodied Energy, MJ/kg 62
52
Embodied Water, L/kg 190
150

Common Calculations

PREN (Pitting Resistance) 26
26
Resilience: Ultimate (Unit Rupture Work), MJ/m3 160
190
Resilience: Unit (Modulus of Resilience), kJ/m3 170
130
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 19
21
Strength to Weight: Bending, points 19
20
Thermal Diffusivity, mm2/s 3.7
4.3
Thermal Shock Resistance, points 13
13

Alloy Composition

Boron (B), % 0
0.0015 to 0.0050
Carbon (C), % 0 to 0.2
0.040 to 0.080
Chromium (Cr), % 23 to 27
16.5 to 18.5
Iron (Fe), % 46.7 to 58
62.8 to 71.5
Manganese (Mn), % 0 to 2.0
0 to 2.0
Molybdenum (Mo), % 0 to 0.5
2.0 to 2.5
Nickel (Ni), % 19 to 22
10 to 13
Nitrogen (N), % 0
0 to 0.1
Phosphorus (P), % 0 to 0.040
0 to 0.035
Silicon (Si), % 0 to 2.0
0 to 1.0
Sulfur (S), % 0 to 0.040
0 to 0.015