ACI-ASTM CK20 Steel vs. EN 1.7213 Steel

Both ACI-ASTM CK20 steel and EN 1.7213 steel are iron alloys. They have 55% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CK20 steel and the bottom bar is EN 1.7213 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 78
73
Tensile Strength: Ultimate (UTS), MPa 530
500 to 1550

Thermal Properties

Latent Heat of Fusion, J/g 310
250
Maximum Temperature: Mechanical, °C 1100
420
Melting Completion (Liquidus), °C 1400
1460
Melting Onset (Solidus), °C 1430
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 14
44
Thermal Expansion, µm/m-K 15
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 2.3
8.4

Otherwise Unclassified Properties

Base Metal Price, % relative 25
2.5
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 4.4
1.5
Embodied Energy, MJ/kg 62
20
Embodied Water, L/kg 190
52

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 19
18 to 55
Strength to Weight: Bending, points 19
18 to 38
Thermal Diffusivity, mm2/s 3.7
12
Thermal Shock Resistance, points 13
15 to 45

Alloy Composition

Carbon (C), % 0 to 0.2
0.22 to 0.29
Chromium (Cr), % 23 to 27
0.9 to 1.2
Copper (Cu), % 0
0 to 0.25
Iron (Fe), % 46.7 to 58
96.7 to 98.1
Manganese (Mn), % 0 to 2.0
0.6 to 0.9
Molybdenum (Mo), % 0 to 0.5
0.15 to 0.3
Nickel (Ni), % 19 to 22
0
Phosphorus (P), % 0 to 0.040
0 to 0.025
Silicon (Si), % 0 to 2.0
0 to 0.3
Sulfur (S), % 0 to 0.040
0.020 to 0.040