MakeItFrom.com
Menu (ESC)

ACI-ASTM CK20 Steel vs. EN 1.7711 Steel

Both ACI-ASTM CK20 steel and EN 1.7711 steel are iron alloys. They have 55% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CK20 steel and the bottom bar is EN 1.7711 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 150
210 to 280
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 37
16 to 22
Fatigue Strength, MPa 220
290 to 520
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 78
73
Tensile Strength: Ultimate (UTS), MPa 530
690 to 930
Tensile Strength: Yield (Proof), MPa 260
400 to 800

Thermal Properties

Latent Heat of Fusion, J/g 310
250
Maximum Temperature: Mechanical, °C 1100
430
Melting Completion (Liquidus), °C 1400
1460
Melting Onset (Solidus), °C 1430
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 14
33
Thermal Expansion, µm/m-K 15
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
7.4
Electrical Conductivity: Equal Weight (Specific), % IACS 2.3
8.5

Otherwise Unclassified Properties

Base Metal Price, % relative 25
3.0
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 4.4
2.3
Embodied Energy, MJ/kg 62
32
Embodied Water, L/kg 190
54

Common Calculations

PREN (Pitting Resistance) 26
2.9
Resilience: Ultimate (Unit Rupture Work), MJ/m3 160
130 to 140
Resilience: Unit (Modulus of Resilience), kJ/m3 170
430 to 1690
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 19
24 to 33
Strength to Weight: Bending, points 19
22 to 27
Thermal Diffusivity, mm2/s 3.7
8.9
Thermal Shock Resistance, points 13
24 to 32

Alloy Composition

Aluminum (Al), % 0
0 to 0.015
Carbon (C), % 0 to 0.2
0.36 to 0.44
Chromium (Cr), % 23 to 27
0.9 to 1.2
Iron (Fe), % 46.7 to 58
96 to 97.5
Manganese (Mn), % 0 to 2.0
0.45 to 0.85
Molybdenum (Mo), % 0 to 0.5
0.5 to 0.65
Nickel (Ni), % 19 to 22
0
Phosphorus (P), % 0 to 0.040
0 to 0.025
Silicon (Si), % 0 to 2.0
0 to 0.4
Sulfur (S), % 0 to 0.040
0 to 0.030
Vanadium (V), % 0
0.25 to 0.35