ACI-ASTM CK20 Steel vs. SAE-AISI 1108 Steel

Both ACI-ASTM CK20 steel and SAE-AISI 1108 steel are iron alloys. They have 53% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CK20 steel and the bottom bar is SAE-AISI 1108 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 150
110 to 140
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 37
23 to 34
Fatigue Strength, MPa 220
170 to 260
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 78
73
Tensile Strength: Ultimate (UTS), MPa 530
380 to 440
Tensile Strength: Yield (Proof), MPa 260
220 to 360

Thermal Properties

Latent Heat of Fusion, J/g 310
250
Maximum Temperature: Mechanical, °C 1100
400
Melting Completion (Liquidus), °C 1400
1460
Melting Onset (Solidus), °C 1430
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 14
52
Thermal Expansion, µm/m-K 15
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
7.0
Electrical Conductivity: Equal Weight (Specific), % IACS 2.3
8.0

Otherwise Unclassified Properties

Base Metal Price, % relative 25
1.8
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 4.4
1.4
Embodied Energy, MJ/kg 62
18
Embodied Water, L/kg 190
46

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 160
95 to 110
Resilience: Unit (Modulus of Resilience), kJ/m3 170
130 to 340
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 19
13 to 16
Strength to Weight: Bending, points 19
15 to 16
Thermal Diffusivity, mm2/s 3.7
14
Thermal Shock Resistance, points 13
12 to 14

Alloy Composition

Carbon (C), % 0 to 0.2
0.080 to 0.13
Chromium (Cr), % 23 to 27
0
Iron (Fe), % 46.7 to 58
98.9 to 99.24
Manganese (Mn), % 0 to 2.0
0.6 to 0.8
Molybdenum (Mo), % 0 to 0.5
0
Nickel (Ni), % 19 to 22
0
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 2.0
0
Sulfur (S), % 0 to 0.040
0.080 to 0.13