ACI-ASTM CN3MN Steel vs. ASTM A182 Grade F5a

Both ACI-ASTM CN3MN steel and ASTM A182 grade F5a are iron alloys. They have 52% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CN3MN steel and the bottom bar is ASTM A182 grade F5a.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
310
Elastic (Young's, Tensile) Modulus, GPa 210
190
Elongation at Break, % 39
25
Fatigue Strength, MPa 250
380
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 80
74
Tensile Strength: Ultimate (UTS), MPa 620
710
Tensile Strength: Yield (Proof), MPa 300
520

Thermal Properties

Latent Heat of Fusion, J/g 310
260
Maximum Temperature: Mechanical, °C 1100
510
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1410
1420
Specific Heat Capacity, J/kg-K 460
470
Thermal Conductivity, W/m-K 13
40
Thermal Expansion, µm/m-K 16
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.8
8.2
Electrical Conductivity: Equal Weight (Specific), % IACS 2.0
9.4

Otherwise Unclassified Properties

Base Metal Price, % relative 33
4.5
Density, g/cm3 8.1
7.8
Embodied Carbon, kg CO2/kg material 6.2
1.8
Embodied Energy, MJ/kg 84
24
Embodied Water, L/kg 200
69

Common Calculations

PREN (Pitting Resistance) 46
6.8
Resilience: Ultimate (Unit Rupture Work), MJ/m3 200
160
Resilience: Unit (Modulus of Resilience), kJ/m3 210
700
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 21
25
Strength to Weight: Bending, points 20
23
Thermal Diffusivity, mm2/s 3.4
11
Thermal Shock Resistance, points 14
20

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.25
Chromium (Cr), % 20 to 22
4.0 to 6.0
Copper (Cu), % 0 to 0.75
0
Iron (Fe), % 41.4 to 50.3
91.4 to 95.6
Manganese (Mn), % 0 to 2.0
0 to 0.6
Molybdenum (Mo), % 6.0 to 7.0
0.44 to 0.65
Nickel (Ni), % 23.5 to 25.5
0 to 0.5
Nitrogen (N), % 0.18 to 0.26
0
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 1.0
0 to 0.5
Sulfur (S), % 0 to 0.010
0 to 0.030