ACI-ASTM CN3MN Steel vs. EN 1.4432 Stainless Steel

Both ACI-ASTM CN3MN steel and EN 1.4432 stainless steel are iron alloys. They have 79% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CN3MN steel and the bottom bar is EN 1.4432 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
190
Elastic (Young's, Tensile) Modulus, GPa 210
200
Elongation at Break, % 39
44
Fatigue Strength, MPa 250
220
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 80
78
Tensile Strength: Ultimate (UTS), MPa 620
610
Tensile Strength: Yield (Proof), MPa 300
250

Thermal Properties

Latent Heat of Fusion, J/g 310
290
Maximum Temperature: Corrosion, °C 430
410
Maximum Temperature: Mechanical, °C 1100
960
Melting Completion (Liquidus), °C 1460
1450
Melting Onset (Solidus), °C 1410
1400
Specific Heat Capacity, J/kg-K 460
470
Thermal Conductivity, W/m-K 13
15
Thermal Expansion, µm/m-K 16
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.8
2.3
Electrical Conductivity: Equal Weight (Specific), % IACS 2.0
2.6

Otherwise Unclassified Properties

Base Metal Price, % relative 33
19
Density, g/cm3 8.1
7.9
Embodied Carbon, kg CO2/kg material 6.2
3.9
Embodied Energy, MJ/kg 84
54
Embodied Water, L/kg 200
150

Common Calculations

PREN (Pitting Resistance) 46
27
Resilience: Ultimate (Unit Rupture Work), MJ/m3 200
220
Resilience: Unit (Modulus of Resilience), kJ/m3 210
150
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 21
21
Strength to Weight: Bending, points 20
20
Thermal Diffusivity, mm2/s 3.4
4.0
Thermal Shock Resistance, points 14
14

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.030
Chromium (Cr), % 20 to 22
16.5 to 18.5
Copper (Cu), % 0 to 0.75
0
Iron (Fe), % 41.4 to 50.3
62.3 to 70.5
Manganese (Mn), % 0 to 2.0
0 to 2.0
Molybdenum (Mo), % 6.0 to 7.0
2.5 to 3.0
Nickel (Ni), % 23.5 to 25.5
10.5 to 13
Nitrogen (N), % 0.18 to 0.26
0 to 0.1
Phosphorus (P), % 0 to 0.040
0 to 0.045
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.010
0 to 0.015