ACI-ASTM CN3MN Steel vs. EN 1.5402 Steel

Both ACI-ASTM CN3MN steel and EN 1.5402 steel are iron alloys. They have 48% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CN3MN steel and the bottom bar is EN 1.5402 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
180
Elastic (Young's, Tensile) Modulus, GPa 210
190
Elongation at Break, % 39
23
Fatigue Strength, MPa 250
260
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 80
73
Tensile Strength: Ultimate (UTS), MPa 620
580
Tensile Strength: Yield (Proof), MPa 300
370

Thermal Properties

Latent Heat of Fusion, J/g 310
250
Maximum Temperature: Mechanical, °C 1100
410
Melting Completion (Liquidus), °C 1460
1470
Melting Onset (Solidus), °C 1410
1420
Specific Heat Capacity, J/kg-K 460
470
Thermal Conductivity, W/m-K 13
51
Thermal Expansion, µm/m-K 16
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.8
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 2.0
8.2

Otherwise Unclassified Properties

Base Metal Price, % relative 33
2.4
Density, g/cm3 8.1
7.9
Embodied Carbon, kg CO2/kg material 6.2
1.7
Embodied Energy, MJ/kg 84
22
Embodied Water, L/kg 200
49

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 200
120
Resilience: Unit (Modulus of Resilience), kJ/m3 210
360
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 21
21
Strength to Weight: Bending, points 20
20
Thermal Diffusivity, mm2/s 3.4
14
Thermal Shock Resistance, points 14
17

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.18
Chromium (Cr), % 20 to 22
0
Copper (Cu), % 0 to 0.75
0
Iron (Fe), % 41.4 to 50.3
97.3 to 98.7
Manganese (Mn), % 0 to 2.0
0.9 to 1.4
Molybdenum (Mo), % 6.0 to 7.0
0.4 to 0.6
Nickel (Ni), % 23.5 to 25.5
0
Nitrogen (N), % 0.18 to 0.26
0
Phosphorus (P), % 0 to 0.040
0 to 0.025
Silicon (Si), % 0 to 1.0
0 to 0.4
Sulfur (S), % 0 to 0.010
0 to 0.015
Vanadium (V), % 0
0.040 to 0.080