ACI-ASTM CN3MN Steel vs. EN 1.6523 Steel

Both ACI-ASTM CN3MN steel and EN 1.6523 steel are iron alloys. They have 48% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CN3MN steel and the bottom bar is EN 1.6523 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
150 to 190
Elastic (Young's, Tensile) Modulus, GPa 210
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 80
73
Tensile Strength: Ultimate (UTS), MPa 620
510 to 1460

Thermal Properties

Latent Heat of Fusion, J/g 310
250
Maximum Temperature: Mechanical, °C 1100
410
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1410
1420
Specific Heat Capacity, J/kg-K 460
470
Thermal Conductivity, W/m-K 13
39
Thermal Expansion, µm/m-K 16
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.8
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 2.0
8.4

Otherwise Unclassified Properties

Base Metal Price, % relative 33
2.6
Density, g/cm3 8.1
7.9
Embodied Carbon, kg CO2/kg material 6.2
1.5
Embodied Energy, MJ/kg 84
20
Embodied Water, L/kg 200
50

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 21
18 to 52
Strength to Weight: Bending, points 20
18 to 36
Thermal Diffusivity, mm2/s 3.4
10
Thermal Shock Resistance, points 14
15 to 43

Alloy Composition

Carbon (C), % 0 to 0.030
0.17 to 0.23
Chromium (Cr), % 20 to 22
0.35 to 0.7
Copper (Cu), % 0 to 0.75
0 to 0.25
Iron (Fe), % 41.4 to 50.3
96.6 to 98.3
Manganese (Mn), % 0 to 2.0
0.65 to 1.0
Molybdenum (Mo), % 6.0 to 7.0
0.15 to 0.25
Nickel (Ni), % 23.5 to 25.5
0.4 to 0.7
Nitrogen (N), % 0.18 to 0.26
0
Phosphorus (P), % 0 to 0.040
0 to 0.025
Silicon (Si), % 0 to 1.0
0 to 0.3
Sulfur (S), % 0 to 0.010
0 to 0.025