ACI-ASTM CN3MN Steel vs. EN 1.8896 Steel

Both ACI-ASTM CN3MN steel and EN 1.8896 steel are iron alloys. They have 47% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CN3MN steel and the bottom bar is EN 1.8896 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
150
Elastic (Young's, Tensile) Modulus, GPa 210
190
Elongation at Break, % 39
24
Fatigue Strength, MPa 250
280
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 80
73
Tensile Strength: Ultimate (UTS), MPa 620
510
Tensile Strength: Yield (Proof), MPa 300
390

Thermal Properties

Latent Heat of Fusion, J/g 310
250
Maximum Temperature: Mechanical, °C 1100
400
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1410
1420
Specific Heat Capacity, J/kg-K 460
470
Thermal Conductivity, W/m-K 13
49
Thermal Expansion, µm/m-K 16
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.8
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 2.0
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 33
2.2
Density, g/cm3 8.1
7.8
Embodied Carbon, kg CO2/kg material 6.2
1.6
Embodied Energy, MJ/kg 84
21
Embodied Water, L/kg 200
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 200
110
Resilience: Unit (Modulus of Resilience), kJ/m3 210
400
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 21
18
Strength to Weight: Bending, points 20
18
Thermal Diffusivity, mm2/s 3.4
13
Thermal Shock Resistance, points 14
15

Alloy Composition

Aluminum (Al), % 0
0.020 to 0.060
Carbon (C), % 0 to 0.030
0 to 0.14
Chromium (Cr), % 20 to 22
0
Copper (Cu), % 0 to 0.75
0
Iron (Fe), % 41.4 to 50.3
97 to 99.98
Manganese (Mn), % 0 to 2.0
0 to 1.5
Molybdenum (Mo), % 6.0 to 7.0
0 to 0.2
Nickel (Ni), % 23.5 to 25.5
0 to 0.3
Niobium (Nb), % 0
0 to 0.050
Nitrogen (N), % 0.18 to 0.26
0 to 0.020
Phosphorus (P), % 0 to 0.040
0 to 0.035
Silicon (Si), % 0 to 1.0
0 to 0.5
Sulfur (S), % 0 to 0.010
0 to 0.030
Titanium (Ti), % 0
0 to 0.050
Vanadium (V), % 0
0 to 0.1