ACI-ASTM CN3MN Steel vs. EN AC-47000 Aluminum

ACI-ASTM CN3MN steel belongs to the iron alloys classification, while EN AC-47000 aluminum belongs to the aluminum alloys. There are 30 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is ACI-ASTM CN3MN steel and the bottom bar is EN AC-47000 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
60
Elastic (Young's, Tensile) Modulus, GPa 210
73
Elongation at Break, % 39
1.7
Fatigue Strength, MPa 250
68
Poisson's Ratio 0.28
0.33
Shear Modulus, GPa 80
27
Tensile Strength: Ultimate (UTS), MPa 620
180
Tensile Strength: Yield (Proof), MPa 300
97

Thermal Properties

Latent Heat of Fusion, J/g 310
570
Maximum Temperature: Mechanical, °C 1100
170
Melting Completion (Liquidus), °C 1460
590
Melting Onset (Solidus), °C 1410
570
Specific Heat Capacity, J/kg-K 460
900
Thermal Conductivity, W/m-K 13
130
Thermal Expansion, µm/m-K 16
21

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.8
33
Electrical Conductivity: Equal Weight (Specific), % IACS 2.0
110

Otherwise Unclassified Properties

Base Metal Price, % relative 33
9.5
Density, g/cm3 8.1
2.6
Embodied Carbon, kg CO2/kg material 6.2
7.7
Embodied Energy, MJ/kg 84
140
Embodied Water, L/kg 200
1040

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 200
2.5
Resilience: Unit (Modulus of Resilience), kJ/m3 210
65
Stiffness to Weight: Axial, points 14
16
Stiffness to Weight: Bending, points 24
54
Strength to Weight: Axial, points 21
19
Strength to Weight: Bending, points 20
27
Thermal Diffusivity, mm2/s 3.4
55
Thermal Shock Resistance, points 14
8.3

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0
82.1 to 89.5
Carbon (C), % 0 to 0.030
0
Chromium (Cr), % 20 to 22
0 to 0.1
Copper (Cu), % 0 to 0.75
0 to 1.0
Iron (Fe), % 41.4 to 50.3
0 to 0.8
Lead (Pb), % 0
0 to 0.2
Magnesium (Mg), % 0
0 to 0.35
Manganese (Mn), % 0 to 2.0
0.050 to 0.55
Molybdenum (Mo), % 6.0 to 7.0
0
Nickel (Ni), % 23.5 to 25.5
0 to 0.3
Nitrogen (N), % 0.18 to 0.26
0
Phosphorus (P), % 0 to 0.040
0
Silicon (Si), % 0 to 1.0
10.5 to 13.5
Sulfur (S), % 0 to 0.010
0
Tin (Sn), % 0
0 to 0.1
Titanium (Ti), % 0
0 to 0.2
Zinc (Zn), % 0
0 to 0.55
Residuals, % 0
0 to 0.25