ACI-ASTM CN3MN Steel vs. CC498K Bronze

ACI-ASTM CN3MN steel belongs to the iron alloys classification, while CC498K bronze belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CN3MN steel and the bottom bar is CC498K bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
78
Elastic (Young's, Tensile) Modulus, GPa 210
110
Elongation at Break, % 39
14
Poisson's Ratio 0.28
0.34
Shear Modulus, GPa 80
41
Tensile Strength: Ultimate (UTS), MPa 620
260
Tensile Strength: Yield (Proof), MPa 300
130

Thermal Properties

Latent Heat of Fusion, J/g 310
190
Maximum Temperature: Mechanical, °C 1100
170
Melting Completion (Liquidus), °C 1460
1000
Melting Onset (Solidus), °C 1410
920
Specific Heat Capacity, J/kg-K 460
370
Thermal Conductivity, W/m-K 13
73
Thermal Expansion, µm/m-K 16
18

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.8
10
Electrical Conductivity: Equal Weight (Specific), % IACS 2.0
10

Otherwise Unclassified Properties

Base Metal Price, % relative 33
32
Density, g/cm3 8.1
8.8
Embodied Carbon, kg CO2/kg material 6.2
3.2
Embodied Energy, MJ/kg 84
52
Embodied Water, L/kg 200
360

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 200
30
Resilience: Unit (Modulus of Resilience), kJ/m3 210
72
Stiffness to Weight: Axial, points 14
6.9
Stiffness to Weight: Bending, points 24
18
Strength to Weight: Axial, points 21
8.1
Strength to Weight: Bending, points 20
10
Thermal Diffusivity, mm2/s 3.4
22
Thermal Shock Resistance, points 14
9.3

Alloy Composition

Aluminum (Al), % 0
0 to 0.010
Antimony (Sb), % 0
0 to 0.25
Carbon (C), % 0 to 0.030
0
Chromium (Cr), % 20 to 22
0
Copper (Cu), % 0 to 0.75
85 to 90
Iron (Fe), % 41.4 to 50.3
0 to 0.25
Lead (Pb), % 0
1.0 to 2.0
Manganese (Mn), % 0 to 2.0
0
Molybdenum (Mo), % 6.0 to 7.0
0
Nickel (Ni), % 23.5 to 25.5
0 to 1.0
Nitrogen (N), % 0.18 to 0.26
0
Phosphorus (P), % 0 to 0.040
0 to 0.050
Silicon (Si), % 0 to 1.0
0 to 0.010
Sulfur (S), % 0 to 0.010
0 to 0.1
Tin (Sn), % 0
5.5 to 6.5
Zinc (Zn), % 0
3.0 to 5.0