ACI-ASTM CN3MN Steel vs. C75700 Nickel Silver

ACI-ASTM CN3MN steel belongs to the iron alloys classification, while C75700 nickel silver belongs to the copper alloys. There are 28 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CN3MN steel and the bottom bar is C75700 nickel silver.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
120
Elongation at Break, % 39
3.2 to 22
Poisson's Ratio 0.28
0.32
Shear Modulus, GPa 80
45
Tensile Strength: Ultimate (UTS), MPa 620
590 to 610
Tensile Strength: Yield (Proof), MPa 300
470 to 580

Thermal Properties

Latent Heat of Fusion, J/g 310
200
Maximum Temperature: Mechanical, °C 1100
180
Melting Completion (Liquidus), °C 1460
1040
Melting Onset (Solidus), °C 1410
990
Specific Heat Capacity, J/kg-K 460
390
Thermal Conductivity, W/m-K 13
40
Thermal Expansion, µm/m-K 16
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.8
8.0
Electrical Conductivity: Equal Weight (Specific), % IACS 2.0
8.6

Otherwise Unclassified Properties

Base Metal Price, % relative 33
30
Density, g/cm3 8.1
8.4
Embodied Carbon, kg CO2/kg material 6.2
3.6
Embodied Energy, MJ/kg 84
56
Embodied Water, L/kg 200
310

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 200
19 to 120
Resilience: Unit (Modulus of Resilience), kJ/m3 210
930 to 1410
Stiffness to Weight: Axial, points 14
7.8
Stiffness to Weight: Bending, points 24
19
Strength to Weight: Axial, points 21
19 to 20
Strength to Weight: Bending, points 20
19
Thermal Diffusivity, mm2/s 3.4
12
Thermal Shock Resistance, points 14
22 to 23

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Carbon (C), % 0 to 0.030
0
Chromium (Cr), % 20 to 22
0
Copper (Cu), % 0 to 0.75
63.5 to 66.5
Iron (Fe), % 41.4 to 50.3
0 to 0.25
Lead (Pb), % 0
0 to 0.050
Manganese (Mn), % 0 to 2.0
0 to 0.5
Molybdenum (Mo), % 6.0 to 7.0
0
Nickel (Ni), % 23.5 to 25.5
11 to 13
Nitrogen (N), % 0.18 to 0.26
0
Phosphorus (P), % 0 to 0.040
0
Silicon (Si), % 0 to 1.0
0
Sulfur (S), % 0 to 0.010
0
Zinc (Zn), % 0
19.2 to 25.5
Residuals, % 0
0 to 0.5