ACI-ASTM CN3MN Steel vs. Z41321 Zinc

ACI-ASTM CN3MN steel belongs to the iron alloys classification, while Z41321 zinc belongs to the zinc alloys. There are 28 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CN3MN steel and the bottom bar is Z41321 zinc.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
87
Elongation at Break, % 39
60
Poisson's Ratio 0.28
0.25
Shear Modulus, GPa 80
35
Tensile Strength: Ultimate (UTS), MPa 620
190
Tensile Strength: Yield (Proof), MPa 300
150

Thermal Properties

Latent Heat of Fusion, J/g 310
110
Maximum Temperature: Mechanical, °C 1100
90
Melting Completion (Liquidus), °C 1460
410
Melting Onset (Solidus), °C 1410
400
Specific Heat Capacity, J/kg-K 460
390
Thermal Conductivity, W/m-K 13
110
Thermal Expansion, µm/m-K 16
26

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.8
27
Electrical Conductivity: Equal Weight (Specific), % IACS 2.0
37

Otherwise Unclassified Properties

Base Metal Price, % relative 33
12
Density, g/cm3 8.1
6.6
Embodied Carbon, kg CO2/kg material 6.2
2.8
Embodied Energy, MJ/kg 84
54
Embodied Water, L/kg 200
340

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 200
100
Resilience: Unit (Modulus of Resilience), kJ/m3 210
130
Stiffness to Weight: Axial, points 14
7.4
Stiffness to Weight: Bending, points 24
23
Strength to Weight: Axial, points 21
7.9
Strength to Weight: Bending, points 20
11
Thermal Diffusivity, mm2/s 3.4
44
Thermal Shock Resistance, points 14
5.9

Alloy Composition

Aluminum (Al), % 0
0 to 0.010
Cadmium (Cd), % 0
0 to 0.0050
Carbon (C), % 0 to 0.030
0
Chromium (Cr), % 20 to 22
0
Copper (Cu), % 0 to 0.75
0.5 to 1.0
Iron (Fe), % 41.4 to 50.3
0 to 0.010
Lead (Pb), % 0
0 to 0.010
Manganese (Mn), % 0 to 2.0
0
Molybdenum (Mo), % 6.0 to 7.0
0
Nickel (Ni), % 23.5 to 25.5
0
Nitrogen (N), % 0.18 to 0.26
0
Phosphorus (P), % 0 to 0.040
0
Silicon (Si), % 0 to 1.0
0
Sulfur (S), % 0 to 0.010
0
Tin (Sn), % 0
0 to 0.0030
Titanium (Ti), % 0
0.080 to 0.18
Zinc (Zn), % 0
98.8 to 99.42