ACI-ASTM CN7MS Steel vs. Grade VDSiCr Steel

Both ACI-ASTM CN7MS steel and grade VDSiCr steel are iron alloys. They have 52% of their average alloy composition in common. There are 23 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CN7MS steel and the bottom bar is grade VDSiCr steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 160
590
Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
80
Tensile Strength: Ultimate (UTS), MPa 540
1950

Thermal Properties

Latent Heat of Fusion, J/g 340
270
Maximum Temperature: Mechanical, °C 1040
410
Melting Completion (Liquidus), °C 1400
1440
Melting Onset (Solidus), °C 1350
1400
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 12
46
Thermal Expansion, µm/m-K 16
13

Otherwise Unclassified Properties

Base Metal Price, % relative 28
2.2
Density, g/cm3 7.9
7.7
Embodied Carbon, kg CO2/kg material 5.1
1.5
Embodied Energy, MJ/kg 71
20
Embodied Water, L/kg 180
48

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 19
70
Strength to Weight: Bending, points 19
45
Thermal Diffusivity, mm2/s 3.2
12
Thermal Shock Resistance, points 13
58

Alloy Composition

Carbon (C), % 0 to 0.070
0.5 to 0.6
Chromium (Cr), % 18 to 20
0.5 to 0.8
Copper (Cu), % 1.5 to 2.0
0 to 0.060
Iron (Fe), % 45.4 to 53.5
96.6 to 97.8
Manganese (Mn), % 0 to 1.0
0.5 to 0.9
Molybdenum (Mo), % 2.5 to 3.0
0
Nickel (Ni), % 22 to 25
0
Phosphorus (P), % 0 to 0.040
0 to 0.025
Silicon (Si), % 2.5 to 3.5
1.2 to 1.6
Sulfur (S), % 0 to 0.030
0 to 0.020