AISI 202 Stainless Steel vs. EN 1.0565 Steel

Both AISI 202 stainless steel and EN 1.0565 steel are iron alloys. They have 70% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is AISI 202 stainless steel and the bottom bar is EN 1.0565 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 210 to 300
160
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 14 to 45
24
Fatigue Strength, MPa 290 to 330
260
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
73
Shear Strength, MPa 490 to 590
350
Tensile Strength: Ultimate (UTS), MPa 700 to 980
550
Tensile Strength: Yield (Proof), MPa 310 to 580
360

Thermal Properties

Latent Heat of Fusion, J/g 290
250
Maximum Temperature: Mechanical, °C 910
400
Melting Completion (Liquidus), °C 1400
1460
Melting Onset (Solidus), °C 1360
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 15
50
Thermal Expansion, µm/m-K 17
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
7.4
Electrical Conductivity: Equal Weight (Specific), % IACS 2.9
8.5

Otherwise Unclassified Properties

Base Metal Price, % relative 13
2.3
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 2.8
1.6
Embodied Energy, MJ/kg 40
22
Embodied Water, L/kg 150
49

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 120 to 260
120
Resilience: Unit (Modulus of Resilience), kJ/m3 250 to 840
340
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 25 to 35
19
Strength to Weight: Bending, points 23 to 29
19
Thermal Diffusivity, mm2/s 4.0
14
Thermal Shock Resistance, points 15 to 21
17

Alloy Composition

Aluminum (Al), % 0
0 to 0.060
Carbon (C), % 0 to 0.15
0 to 0.2
Chromium (Cr), % 17 to 19
0 to 0.3
Copper (Cu), % 0
0 to 0.3
Iron (Fe), % 63.5 to 71.5
96.2 to 99
Manganese (Mn), % 7.5 to 10
0.9 to 1.7
Molybdenum (Mo), % 0
0 to 0.080
Nickel (Ni), % 4.0 to 6.0
0 to 0.5
Niobium (Nb), % 0
0 to 0.050
Nitrogen (N), % 0 to 0.25
0 to 0.020
Phosphorus (P), % 0 to 0.060
0 to 0.025
Silicon (Si), % 0 to 1.0
0 to 0.5
Sulfur (S), % 0 to 0.030
0 to 0.015
Titanium (Ti), % 0
0 to 0.030
Vanadium (V), % 0
0 to 0.1