AISI 202 Stainless Steel vs. CC334G Bronze
AISI 202 stainless steel belongs to the iron alloys classification, while CC334G bronze belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is AISI 202 stainless steel and the bottom bar is CC334G bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 210 to 300 | |
| 210 |
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 120 |
| Elongation at Break, % | 14 to 45 | |
| 5.6 |
| Poisson's Ratio | 0.28 | |
| 0.33 |
| Shear Modulus, GPa | 77 | |
| 45 |
| Tensile Strength: Ultimate (UTS), MPa | 700 to 980 | |
| 810 |
| Tensile Strength: Yield (Proof), MPa | 310 to 580 | |
| 410 |
Thermal Properties
| Latent Heat of Fusion, J/g | 290 | |
| 240 |
| Maximum Temperature: Mechanical, °C | 910 | |
| 240 |
| Melting Completion (Liquidus), °C | 1400 | |
| 1080 |
| Melting Onset (Solidus), °C | 1360 | |
| 1020 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 450 |
| Thermal Conductivity, W/m-K | 15 | |
| 41 |
| Thermal Expansion, µm/m-K | 17 | |
| 18 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.4 | |
| 7.3 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.9 | |
| 8.0 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 13 | |
| 29 |
| Density, g/cm3 | 7.7 | |
| 8.2 |
| Embodied Carbon, kg CO2/kg material | 2.8 | |
| 3.6 |
| Embodied Energy, MJ/kg | 40 | |
| 59 |
| Embodied Water, L/kg | 150 | |
| 390 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 120 to 260 | |
| 38 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 250 to 840 | |
| 710 |
| Stiffness to Weight: Axial, points | 14 | |
| 8.1 |
| Stiffness to Weight: Bending, points | 25 | |
| 20 |
| Strength to Weight: Axial, points | 25 to 35 | |
| 28 |
| Strength to Weight: Bending, points | 23 to 29 | |
| 24 |
| Thermal Diffusivity, mm2/s | 4.0 | |
| 11 |
| Thermal Shock Resistance, points | 15 to 21 | |
| 28 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 10 to 12 |
| Carbon (C), % | 0 to 0.15 | |
| 0 |
| Chromium (Cr), % | 17 to 19 | |
| 0 |
| Copper (Cu), % | 0 | |
| 72 to 84.5 |
| Iron (Fe), % | 63.5 to 71.5 | |
| 3.0 to 7.0 |
| Lead (Pb), % | 0 | |
| 0 to 0.050 |
| Magnesium (Mg), % | 0 | |
| 0 to 0.050 |
| Manganese (Mn), % | 7.5 to 10 | |
| 0 to 2.5 |
| Nickel (Ni), % | 4.0 to 6.0 | |
| 4.0 to 7.5 |
| Nitrogen (N), % | 0 to 0.25 | |
| 0 |
| Phosphorus (P), % | 0 to 0.060 | |
| 0 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 to 0.1 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 |
| Tin (Sn), % | 0 | |
| 0 to 0.2 |
| Zinc (Zn), % | 0 | |
| 0 to 0.5 |