AISI 301L Stainless Steel vs. C31400 Bronze
AISI 301L stainless steel belongs to the iron alloys classification, while C31400 bronze belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is AISI 301L stainless steel and the bottom bar is C31400 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 110 |
| Elongation at Break, % | 22 to 50 | |
| 6.8 to 29 |
| Poisson's Ratio | 0.28 | |
| 0.33 |
| Shear Modulus, GPa | 77 | |
| 42 |
| Shear Strength, MPa | 440 to 660 | |
| 180 to 240 |
| Tensile Strength: Ultimate (UTS), MPa | 620 to 1040 | |
| 270 to 420 |
| Tensile Strength: Yield (Proof), MPa | 250 to 790 | |
| 78 to 310 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 200 |
| Maximum Temperature: Mechanical, °C | 890 | |
| 180 |
| Melting Completion (Liquidus), °C | 1430 | |
| 1040 |
| Melting Onset (Solidus), °C | 1390 | |
| 1010 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 380 |
| Thermal Conductivity, W/m-K | 15 | |
| 180 |
| Thermal Expansion, µm/m-K | 16 | |
| 18 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.3 | |
| 42 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.7 | |
| 43 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 13 | |
| 29 |
| Density, g/cm3 | 7.8 | |
| 8.8 |
| Embodied Carbon, kg CO2/kg material | 2.7 | |
| 2.6 |
| Embodied Energy, MJ/kg | 39 | |
| 42 |
| Embodied Water, L/kg | 130 | |
| 310 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 210 to 300 | |
| 26 to 59 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 160 to 1580 | |
| 28 to 420 |
| Stiffness to Weight: Axial, points | 14 | |
| 7.1 |
| Stiffness to Weight: Bending, points | 25 | |
| 18 |
| Strength to Weight: Axial, points | 22 to 37 | |
| 8.7 to 13 |
| Strength to Weight: Bending, points | 21 to 29 | |
| 11 to 14 |
| Thermal Diffusivity, mm2/s | 4.1 | |
| 54 |
| Thermal Shock Resistance, points | 14 to 24 | |
| 9.6 to 15 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Carbon (C), % | 0 to 0.030 | |
| 0 |
| Chromium (Cr), % | 16 to 18 | |
| 0 |
| Copper (Cu), % | 0 | |
| 87.5 to 90.5 |
| Iron (Fe), % | 70.7 to 78 | |
| 0 to 0.1 |
| Lead (Pb), % | 0 | |
| 1.3 to 2.5 |
| Manganese (Mn), % | 0 to 2.0 | |
| 0 |
| Nickel (Ni), % | 6.0 to 8.0 | |
| 0 to 0.7 |
| Nitrogen (N), % | 0 to 0.2 | |
| 0 |
| Phosphorus (P), % | 0 to 0.045 | |
| 0 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 5.8 to 11.2 |
| Residuals, % | 0 | |
| 0 to 0.4 |