AISI 302 Stainless Steel vs. SAE-AISI M47 Steel

Both AISI 302 stainless steel and SAE-AISI M47 steel are iron alloys. They have 76% of their average alloy composition in common. There are 22 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is AISI 302 stainless steel and the bottom bar is SAE-AISI M47 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
77
Tensile Strength: Ultimate (UTS), MPa 580 to 1430
810 to 2310

Thermal Properties

Latent Heat of Fusion, J/g 280
270
Melting Completion (Liquidus), °C 1420
1540
Melting Onset (Solidus), °C 1400
1500
Specific Heat Capacity, J/kg-K 480
450
Thermal Conductivity, W/m-K 16
23
Thermal Expansion, µm/m-K 17
11

Otherwise Unclassified Properties

Base Metal Price, % relative 15
26
Density, g/cm3 7.8
8.1
Embodied Carbon, kg CO2/kg material 3.0
7.4
Embodied Energy, MJ/kg 42
100
Embodied Water, L/kg 140
120

Common Calculations

PREN (Pitting Resistance) 19
38
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 21 to 51
28 to 79
Strength to Weight: Bending, points 20 to 36
24 to 48
Thermal Diffusivity, mm2/s 4.4
6.3
Thermal Shock Resistance, points 12 to 31
27 to 77

Alloy Composition

Carbon (C), % 0 to 0.15
1.1 to 1.2
Chromium (Cr), % 17 to 19
3.5 to 4.0
Cobalt (Co), % 0
4.8 to 5.3
Copper (Cu), % 0
0 to 0.25
Iron (Fe), % 67.9 to 75
78.7 to 85
Manganese (Mn), % 0 to 2.0
0.15 to 0.4
Molybdenum (Mo), % 0
9.3 to 10
Nickel (Ni), % 8.0 to 10
0 to 0.3
Nitrogen (N), % 0 to 0.1
0
Phosphorus (P), % 0 to 0.045
0 to 0.030
Silicon (Si), % 0 to 0.75
0.2 to 0.45
Sulfur (S), % 0 to 0.030
0 to 0.030
Tungsten (W), % 0
1.3 to 1.8
Vanadium (V), % 0
1.2 to 1.4

Comparable Variants