AISI 302B Stainless Steel vs. EN 1.0050 Steel

Both AISI 302B stainless steel and EN 1.0050 steel are iron alloys. They have 69% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is AISI 302B stainless steel and the bottom bar is EN 1.0050 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
150
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 45
18
Fatigue Strength, MPa 210
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
73
Shear Strength, MPa 410
330
Tensile Strength: Ultimate (UTS), MPa 580
530
Tensile Strength: Yield (Proof), MPa 230
280

Thermal Properties

Latent Heat of Fusion, J/g 320
250
Maximum Temperature: Mechanical, °C 930
400
Melting Completion (Liquidus), °C 1400
1470
Melting Onset (Solidus), °C 1360
1430
Specific Heat Capacity, J/kg-K 490
470
Thermal Conductivity, W/m-K 17
53
Thermal Expansion, µm/m-K 16
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
6.8
Electrical Conductivity: Equal Weight (Specific), % IACS 2.6
7.8

Otherwise Unclassified Properties

Base Metal Price, % relative 15
1.7
Density, g/cm3 7.7
7.9
Embodied Carbon, kg CO2/kg material 3.0
1.4
Embodied Energy, MJ/kg 43
18
Embodied Water, L/kg 140
45

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 210
81
Resilience: Unit (Modulus of Resilience), kJ/m3 140
210
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 21
19
Strength to Weight: Bending, points 20
18
Thermal Diffusivity, mm2/s 4.4
14
Thermal Shock Resistance, points 13
17

Alloy Composition

Carbon (C), % 0 to 0.15
0
Chromium (Cr), % 17 to 19
0
Iron (Fe), % 65.7 to 73
99.876 to 100
Manganese (Mn), % 0 to 2.0
0
Nickel (Ni), % 8.0 to 10
0
Nitrogen (N), % 0 to 0.1
0 to 0.014
Phosphorus (P), % 0 to 0.045
0 to 0.055
Silicon (Si), % 2.0 to 3.0
0
Sulfur (S), % 0 to 0.030
0 to 0.055