AISI 303Se Stainless Steel vs. EN 1.8903 Steel

Both AISI 303Se stainless steel and EN 1.8903 steel are iron alloys. They have 73% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is AISI 303Se stainless steel and the bottom bar is EN 1.8903 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
190
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 45
19
Fatigue Strength, MPa 210
330
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
73
Shear Strength, MPa 410
390
Tensile Strength: Ultimate (UTS), MPa 590
630
Tensile Strength: Yield (Proof), MPa 230
480

Thermal Properties

Latent Heat of Fusion, J/g 290
250
Maximum Temperature: Mechanical, °C 930
410
Melting Completion (Liquidus), °C 1420
1460
Melting Onset (Solidus), °C 1380
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 16
46
Thermal Expansion, µm/m-K 16
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
7.6
Electrical Conductivity: Equal Weight (Specific), % IACS 2.8
8.7

Otherwise Unclassified Properties

Base Metal Price, % relative 16
2.6
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 3.0
1.8
Embodied Energy, MJ/kg 42
24
Embodied Water, L/kg 140
51

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 210
110
Resilience: Unit (Modulus of Resilience), kJ/m3 130
620
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 21
22
Strength to Weight: Bending, points 20
21
Thermal Diffusivity, mm2/s 4.3
12
Thermal Shock Resistance, points 13
18

Alloy Composition

Aluminum (Al), % 0
0 to 0.015
Carbon (C), % 0 to 0.15
0 to 0.22
Chromium (Cr), % 17 to 19
0 to 0.35
Copper (Cu), % 0
0 to 0.6
Iron (Fe), % 67.2 to 74.9
95 to 99.05
Manganese (Mn), % 0 to 2.0
1.0 to 1.8
Molybdenum (Mo), % 0
0 to 0.13
Nickel (Ni), % 8.0 to 10
0 to 0.85
Niobium (Nb), % 0
0 to 0.060
Nitrogen (N), % 0
0 to 0.027
Phosphorus (P), % 0 to 0.2
0 to 0.030
Selenium (Se), % 0.15 to 0.35
0
Silicon (Si), % 0 to 1.0
0 to 0.65
Sulfur (S), % 0 to 0.060
0 to 0.025
Titanium (Ti), % 0
0 to 0.060
Vanadium (V), % 0
0 to 0.22