AISI 304 Stainless Steel vs. EN 1.0050 Steel

Both AISI 304 stainless steel and EN 1.0050 steel are iron alloys. They have 70% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is AISI 304 stainless steel and the bottom bar is EN 1.0050 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 170 to 360
150
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 8.0 to 43
18
Fatigue Strength, MPa 210 to 440
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
73
Shear Strength, MPa 400 to 690
330
Tensile Strength: Ultimate (UTS), MPa 580 to 1180
530
Tensile Strength: Yield (Proof), MPa 230 to 860
280

Thermal Properties

Latent Heat of Fusion, J/g 290
250
Maximum Temperature: Mechanical, °C 710
400
Melting Completion (Liquidus), °C 1450
1470
Melting Onset (Solidus), °C 1400
1430
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 16
53
Thermal Expansion, µm/m-K 17
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
6.8
Electrical Conductivity: Equal Weight (Specific), % IACS 2.7
7.8

Otherwise Unclassified Properties

Base Metal Price, % relative 15
1.7
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 3.0
1.4
Embodied Energy, MJ/kg 43
18
Embodied Water, L/kg 150
45

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 86 to 250
81
Resilience: Unit (Modulus of Resilience), kJ/m3 140 to 1870
210
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 21 to 42
19
Strength to Weight: Bending, points 20 to 32
18
Thermal Diffusivity, mm2/s 4.2
14
Thermal Shock Resistance, points 12 to 25
17

Alloy Composition

Carbon (C), % 0 to 0.080
0
Chromium (Cr), % 18 to 20
0
Iron (Fe), % 66.5 to 74
99.876 to 100
Manganese (Mn), % 0 to 2.0
0
Nickel (Ni), % 8.0 to 10.5
0
Nitrogen (N), % 0 to 0.1
0 to 0.014
Phosphorus (P), % 0 to 0.045
0 to 0.055
Silicon (Si), % 0 to 0.75
0
Sulfur (S), % 0 to 0.030
0 to 0.055