AISI 304L Stainless Steel vs. 92-silver 8-tin-oxide
AISI 304L stainless steel belongs to the iron alloys classification, while 92-silver 8-tin-oxide belongs to the otherwise unclassified metals. There are 6 material properties with values for both materials. Properties with values for just one material (29, in this case) are not shown.
For each property being compared, the top bar is AISI 304L stainless steel and the bottom bar is 92-silver 8-tin-oxide.
Metric UnitsUS Customary Units
Material Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.4 | |
| 76 to 80 |
| Elongation at Break, % | 6.7 to 46 | |
| 32 to 34 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 71 to 240 | |
| 62 to 110 |
| Shear Strength, MPa | 370 to 680 | |
| 150 to 210 |
| Tensile Strength: Ultimate (UTS), MPa | 540 to 1160 | |
| 230 to 320 |
| Tensile Strength: Yield (Proof), MPa | 190 to 870 | |
| 120 to 300 |