AISI 304L Stainless Steel vs. ASTM A148 Cast Steel

Both AISI 304L stainless steel and ASTM A148 cast steel are iron alloys. There are 30 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is AISI 304L stainless steel and the bottom bar is ASTM A148 cast steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 160 to 350
190 to 390
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 6.7 to 46
5.7 to 25
Fatigue Strength, MPa 170 to 430
280 to 670
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
73
Tensile Strength: Ultimate (UTS), MPa 540 to 1160
630 to 1300
Tensile Strength: Yield (Proof), MPa 190 to 870
390 to 1160

Thermal Properties

Latent Heat of Fusion, J/g 290
250
Maximum Temperature: Mechanical, °C 540
400 to 430
Melting Completion (Liquidus), °C 1450
1460
Melting Onset (Solidus), °C 1400
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 16
37 to 47
Thermal Expansion, µm/m-K 17
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
7.3 to 7.5
Electrical Conductivity: Equal Weight (Specific), % IACS 2.7
8.3 to 8.6

Otherwise Unclassified Properties

Base Metal Price, % relative 16
2.3 to 3.3
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 3.1
1.5 to 1.7
Embodied Energy, MJ/kg 44
20 to 22
Embodied Water, L/kg 150
48 to 53

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 71 to 240
71 to 150
Resilience: Unit (Modulus of Resilience), kJ/m3 92 to 1900
400 to 3570
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 19 to 41
22 to 46
Strength to Weight: Bending, points 19 to 31
21 to 34
Thermal Diffusivity, mm2/s 4.2
9.9 to 13
Thermal Shock Resistance, points 12 to 25
18 to 38

Comparable Variants