AISI 304L Stainless Steel vs. ASTM A372 Grade E Steel

Both AISI 304L stainless steel and ASTM A372 grade E steel are iron alloys. They have 71% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is AISI 304L stainless steel and the bottom bar is ASTM A372 grade E steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 160 to 350
200 to 280
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 6.7 to 46
20 to 22
Fatigue Strength, MPa 170 to 430
310 to 380
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
73
Shear Strength, MPa 370 to 680
410 to 570
Tensile Strength: Ultimate (UTS), MPa 540 to 1160
650 to 910
Tensile Strength: Yield (Proof), MPa 190 to 870
430 to 550

Thermal Properties

Latent Heat of Fusion, J/g 290
250
Maximum Temperature: Mechanical, °C 540
420
Melting Completion (Liquidus), °C 1450
1460
Melting Onset (Solidus), °C 1400
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 16
44
Thermal Expansion, µm/m-K 17
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 2.7
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 16
2.4
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 3.1
1.5
Embodied Energy, MJ/kg 44
20
Embodied Water, L/kg 150
51

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 71 to 240
130 to 160
Resilience: Unit (Modulus of Resilience), kJ/m3 92 to 1900
500 to 810
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 19 to 41
23 to 32
Strength to Weight: Bending, points 19 to 31
21 to 27
Thermal Diffusivity, mm2/s 4.2
12
Thermal Shock Resistance, points 12 to 25
19 to 27

Alloy Composition

Carbon (C), % 0 to 0.030
0.25 to 0.35
Chromium (Cr), % 18 to 20
0.8 to 1.2
Iron (Fe), % 65 to 74
97 to 98.3
Manganese (Mn), % 0 to 2.0
0.4 to 0.9
Molybdenum (Mo), % 0
0.15 to 0.25
Nickel (Ni), % 8.0 to 12
0
Nitrogen (N), % 0 to 0.1
0
Phosphorus (P), % 0 to 0.045
0 to 0.015
Silicon (Si), % 0 to 0.75
0.15 to 0.35
Sulfur (S), % 0 to 0.030
0 to 0.010