AISI 304L Stainless Steel vs. EN 1.4508 Stainless Steel

Both AISI 304L stainless steel and EN 1.4508 stainless steel are iron alloys. They have a very high 96% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is AISI 304L stainless steel and the bottom bar is EN 1.4508 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 6.7 to 46
34
Fatigue Strength, MPa 170 to 430
210
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 77
79
Tensile Strength: Ultimate (UTS), MPa 540 to 1160
570
Tensile Strength: Yield (Proof), MPa 190 to 870
260

Thermal Properties

Latent Heat of Fusion, J/g 290
300
Maximum Temperature: Corrosion, °C 420
420
Maximum Temperature: Mechanical, °C 540
1000
Melting Completion (Liquidus), °C 1450
1450
Melting Onset (Solidus), °C 1400
1400
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 16
15
Thermal Expansion, µm/m-K 17
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
2.1
Electrical Conductivity: Equal Weight (Specific), % IACS 2.7
2.4

Otherwise Unclassified Properties

Base Metal Price, % relative 16
20
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 3.1
4.0
Embodied Energy, MJ/kg 44
55
Embodied Water, L/kg 150
160

Common Calculations

PREN (Pitting Resistance) 20
32
Resilience: Ultimate (Unit Rupture Work), MJ/m3 71 to 240
160
Resilience: Unit (Modulus of Resilience), kJ/m3 92 to 1900
170
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 19 to 41
20
Strength to Weight: Bending, points 19 to 31
19
Thermal Diffusivity, mm2/s 4.2
4.1
Thermal Shock Resistance, points 12 to 25
17

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.030
Chromium (Cr), % 18 to 20
18 to 20
Iron (Fe), % 65 to 74
61.2 to 69.9
Manganese (Mn), % 0 to 2.0
0 to 1.5
Molybdenum (Mo), % 0
3.0 to 3.5
Nickel (Ni), % 8.0 to 12
9.0 to 12
Nitrogen (N), % 0 to 0.1
0.1 to 0.2
Phosphorus (P), % 0 to 0.045
0 to 0.040
Silicon (Si), % 0 to 0.75
0 to 1.5
Sulfur (S), % 0 to 0.030
0 to 0.030