AISI 304L Stainless Steel vs. EN 1.4848 Stainless Steel

Both AISI 304L stainless steel and EN 1.4848 stainless steel are iron alloys. They have 81% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is AISI 304L stainless steel and the bottom bar is EN 1.4848 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 160 to 350
150
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 6.7 to 46
9.0
Fatigue Strength, MPa 170 to 430
130
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 77
78
Tensile Strength: Ultimate (UTS), MPa 540 to 1160
510
Tensile Strength: Yield (Proof), MPa 190 to 870
250

Thermal Properties

Latent Heat of Fusion, J/g 290
320
Maximum Temperature: Corrosion, °C 420
440
Maximum Temperature: Mechanical, °C 540
1100
Melting Completion (Liquidus), °C 1450
1390
Melting Onset (Solidus), °C 1400
1340
Specific Heat Capacity, J/kg-K 480
490
Thermal Conductivity, W/m-K 16
15
Thermal Expansion, µm/m-K 17
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
2.0
Electrical Conductivity: Equal Weight (Specific), % IACS 2.7
2.3

Otherwise Unclassified Properties

Base Metal Price, % relative 16
25
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 3.1
4.4
Embodied Energy, MJ/kg 44
63
Embodied Water, L/kg 150
200

Common Calculations

PREN (Pitting Resistance) 20
26
Resilience: Ultimate (Unit Rupture Work), MJ/m3 71 to 240
38
Resilience: Unit (Modulus of Resilience), kJ/m3 92 to 1900
150
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 19 to 41
18
Strength to Weight: Bending, points 19 to 31
18
Thermal Diffusivity, mm2/s 4.2
3.9
Thermal Shock Resistance, points 12 to 25
11

Alloy Composition

Carbon (C), % 0 to 0.030
0.3 to 0.5
Chromium (Cr), % 18 to 20
24 to 27
Iron (Fe), % 65 to 74
45.4 to 55.7
Manganese (Mn), % 0 to 2.0
0 to 2.0
Molybdenum (Mo), % 0
0 to 0.5
Nickel (Ni), % 8.0 to 12
19 to 22
Nitrogen (N), % 0 to 0.1
0
Phosphorus (P), % 0 to 0.045
0 to 0.040
Silicon (Si), % 0 to 0.75
1.0 to 2.5
Sulfur (S), % 0 to 0.030
0 to 0.030