AISI 304L Stainless Steel vs. EN 1.5508 Steel

Both AISI 304L stainless steel and EN 1.5508 steel are iron alloys. They have 71% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is AISI 304L stainless steel and the bottom bar is EN 1.5508 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 160 to 350
130 to 180
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 6.7 to 46
11 to 20
Fatigue Strength, MPa 170 to 430
210 to 320
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
73
Shear Strength, MPa 370 to 680
300 to 360
Tensile Strength: Ultimate (UTS), MPa 540 to 1160
420 to 1460
Tensile Strength: Yield (Proof), MPa 190 to 870
310 to 490

Thermal Properties

Latent Heat of Fusion, J/g 290
250
Maximum Temperature: Mechanical, °C 540
400
Melting Completion (Liquidus), °C 1450
1460
Melting Onset (Solidus), °C 1400
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 16
51
Thermal Expansion, µm/m-K 17
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 2.7
8.2

Otherwise Unclassified Properties

Base Metal Price, % relative 16
1.9
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 3.1
1.4
Embodied Energy, MJ/kg 44
19
Embodied Water, L/kg 150
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 71 to 240
44 to 230
Resilience: Unit (Modulus of Resilience), kJ/m3 92 to 1900
260 to 640
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 19 to 41
15 to 52
Strength to Weight: Bending, points 19 to 31
16 to 36
Thermal Diffusivity, mm2/s 4.2
14
Thermal Shock Resistance, points 12 to 25
12 to 43

Alloy Composition

Boron (B), % 0
0.00080 to 0.0050
Carbon (C), % 0 to 0.030
0.2 to 0.25
Chromium (Cr), % 18 to 20
0 to 0.3
Copper (Cu), % 0
0 to 0.25
Iron (Fe), % 65 to 74
97.9 to 99.199
Manganese (Mn), % 0 to 2.0
0.6 to 0.9
Nickel (Ni), % 8.0 to 12
0
Nitrogen (N), % 0 to 0.1
0
Phosphorus (P), % 0 to 0.045
0 to 0.025
Silicon (Si), % 0 to 0.75
0 to 0.3
Sulfur (S), % 0 to 0.030
0 to 0.025

Comparable Variants