AISI 304L Stainless Steel vs. EN 1.7220 Steel

Both AISI 304L stainless steel and EN 1.7220 steel are iron alloys. They have 72% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is AISI 304L stainless steel and the bottom bar is EN 1.7220 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 160 to 350
160 to 290
Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
73
Tensile Strength: Ultimate (UTS), MPa 540 to 1160
520 to 1720

Thermal Properties

Latent Heat of Fusion, J/g 290
250
Maximum Temperature: Mechanical, °C 540
420
Melting Completion (Liquidus), °C 1450
1460
Melting Onset (Solidus), °C 1400
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 16
44
Thermal Expansion, µm/m-K 17
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 2.7
8.4

Otherwise Unclassified Properties

Base Metal Price, % relative 16
2.5
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 3.1
1.5
Embodied Energy, MJ/kg 44
20
Embodied Water, L/kg 150
51

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 19 to 41
18 to 61
Strength to Weight: Bending, points 19 to 31
18 to 41
Thermal Diffusivity, mm2/s 4.2
12
Thermal Shock Resistance, points 12 to 25
15 to 50

Alloy Composition

Carbon (C), % 0 to 0.030
0.3 to 0.37
Chromium (Cr), % 18 to 20
0.9 to 1.2
Iron (Fe), % 65 to 74
96.8 to 98.1
Manganese (Mn), % 0 to 2.0
0.6 to 0.9
Molybdenum (Mo), % 0
0.15 to 0.3
Nickel (Ni), % 8.0 to 12
0
Nitrogen (N), % 0 to 0.1
0
Phosphorus (P), % 0 to 0.045
0 to 0.035
Silicon (Si), % 0 to 0.75
0 to 0.4
Sulfur (S), % 0 to 0.030
0 to 0.035