AISI 304L Stainless Steel vs. EN 1.7357 Steel

Both AISI 304L stainless steel and EN 1.7357 steel are iron alloys. They have 72% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is AISI 304L stainless steel and the bottom bar is EN 1.7357 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 160 to 350
180
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 6.7 to 46
23
Fatigue Strength, MPa 170 to 430
260
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
73
Tensile Strength: Ultimate (UTS), MPa 540 to 1160
590
Tensile Strength: Yield (Proof), MPa 190 to 870
360

Thermal Properties

Latent Heat of Fusion, J/g 290
250
Maximum Temperature: Mechanical, °C 540
430
Melting Completion (Liquidus), °C 1450
1460
Melting Onset (Solidus), °C 1400
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 16
41
Thermal Expansion, µm/m-K 17
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
7.4
Electrical Conductivity: Equal Weight (Specific), % IACS 2.7
8.5

Otherwise Unclassified Properties

Base Metal Price, % relative 16
2.9
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 3.1
1.6
Embodied Energy, MJ/kg 44
21
Embodied Water, L/kg 150
53

Common Calculations

PREN (Pitting Resistance) 20
3.1
Resilience: Ultimate (Unit Rupture Work), MJ/m3 71 to 240
120
Resilience: Unit (Modulus of Resilience), kJ/m3 92 to 1900
340
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 19 to 41
21
Strength to Weight: Bending, points 19 to 31
20
Thermal Diffusivity, mm2/s 4.2
11
Thermal Shock Resistance, points 12 to 25
17

Alloy Composition

Carbon (C), % 0 to 0.030
0.15 to 0.2
Chromium (Cr), % 18 to 20
1.0 to 1.5
Iron (Fe), % 65 to 74
96 to 97.9
Manganese (Mn), % 0 to 2.0
0.5 to 1.0
Molybdenum (Mo), % 0
0.45 to 0.65
Nickel (Ni), % 8.0 to 12
0
Nitrogen (N), % 0 to 0.1
0
Phosphorus (P), % 0 to 0.045
0 to 0.025
Silicon (Si), % 0 to 0.75
0 to 0.6
Sulfur (S), % 0 to 0.030
0 to 0.030