AISI 304L Stainless Steel vs. EN 1.8888 Steel

Both AISI 304L stainless steel and EN 1.8888 steel are iron alloys. They have 73% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is AISI 304L stainless steel and the bottom bar is EN 1.8888 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 160 to 350
250
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 6.7 to 46
16
Fatigue Strength, MPa 170 to 430
470
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
73
Shear Strength, MPa 370 to 680
510
Tensile Strength: Ultimate (UTS), MPa 540 to 1160
830
Tensile Strength: Yield (Proof), MPa 190 to 870
720

Thermal Properties

Latent Heat of Fusion, J/g 290
260
Maximum Temperature: Mechanical, °C 540
420
Melting Completion (Liquidus), °C 1450
1460
Melting Onset (Solidus), °C 1400
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 16
40
Thermal Expansion, µm/m-K 17
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
8.1
Electrical Conductivity: Equal Weight (Specific), % IACS 2.7
9.3

Otherwise Unclassified Properties

Base Metal Price, % relative 16
3.7
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 3.1
1.9
Embodied Energy, MJ/kg 44
26
Embodied Water, L/kg 150
54

Common Calculations

PREN (Pitting Resistance) 20
2.0
Resilience: Ultimate (Unit Rupture Work), MJ/m3 71 to 240
130
Resilience: Unit (Modulus of Resilience), kJ/m3 92 to 1900
1370
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 19 to 41
29
Strength to Weight: Bending, points 19 to 31
25
Thermal Diffusivity, mm2/s 4.2
11
Thermal Shock Resistance, points 12 to 25
24

Alloy Composition

Boron (B), % 0
0 to 0.0050
Carbon (C), % 0 to 0.030
0 to 0.2
Chromium (Cr), % 18 to 20
0 to 1.5
Copper (Cu), % 0
0 to 0.3
Iron (Fe), % 65 to 74
91.9 to 100
Manganese (Mn), % 0 to 2.0
0 to 1.7
Molybdenum (Mo), % 0
0 to 0.7
Nickel (Ni), % 8.0 to 12
0 to 2.5
Niobium (Nb), % 0
0 to 0.060
Nitrogen (N), % 0 to 0.1
0 to 0.015
Phosphorus (P), % 0 to 0.045
0 to 0.020
Silicon (Si), % 0 to 0.75
0 to 0.8
Sulfur (S), % 0 to 0.030
0 to 0.0050
Titanium (Ti), % 0
0 to 0.050
Vanadium (V), % 0
0 to 0.12
Zirconium (Zr), % 0
0 to 0.15