AISI 304L Stainless Steel vs. CC493K Bronze
AISI 304L stainless steel belongs to the iron alloys classification, while CC493K bronze belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is AISI 304L stainless steel and the bottom bar is CC493K bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 160 to 350 | |
| 74 |
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 100 |
| Elongation at Break, % | 6.7 to 46 | |
| 14 |
| Poisson's Ratio | 0.28 | |
| 0.34 |
| Shear Modulus, GPa | 77 | |
| 39 |
| Tensile Strength: Ultimate (UTS), MPa | 540 to 1160 | |
| 270 |
| Tensile Strength: Yield (Proof), MPa | 190 to 870 | |
| 140 |
Thermal Properties
| Latent Heat of Fusion, J/g | 290 | |
| 180 |
| Maximum Temperature: Mechanical, °C | 540 | |
| 160 |
| Melting Completion (Liquidus), °C | 1450 | |
| 960 |
| Melting Onset (Solidus), °C | 1400 | |
| 880 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 360 |
| Thermal Conductivity, W/m-K | 16 | |
| 61 |
| Thermal Expansion, µm/m-K | 17 | |
| 19 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.4 | |
| 12 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.7 | |
| 12 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 16 | |
| 32 |
| Density, g/cm3 | 7.8 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 3.1 | |
| 3.3 |
| Embodied Energy, MJ/kg | 44 | |
| 53 |
| Embodied Water, L/kg | 150 | |
| 370 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 71 to 240 | |
| 33 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 92 to 1900 | |
| 89 |
| Stiffness to Weight: Axial, points | 14 | |
| 6.5 |
| Stiffness to Weight: Bending, points | 25 | |
| 18 |
| Strength to Weight: Axial, points | 19 to 41 | |
| 8.6 |
| Strength to Weight: Bending, points | 19 to 31 | |
| 11 |
| Thermal Diffusivity, mm2/s | 4.2 | |
| 19 |
| Thermal Shock Resistance, points | 12 to 25 | |
| 10 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.010 |
| Antimony (Sb), % | 0 | |
| 0 to 0.3 |
| Carbon (C), % | 0 to 0.030 | |
| 0 |
| Chromium (Cr), % | 18 to 20 | |
| 0 |
| Copper (Cu), % | 0 | |
| 79 to 86 |
| Iron (Fe), % | 65 to 74 | |
| 0 to 0.2 |
| Lead (Pb), % | 0 | |
| 5.0 to 8.0 |
| Manganese (Mn), % | 0 to 2.0 | |
| 0 |
| Nickel (Ni), % | 8.0 to 12 | |
| 0 to 2.0 |
| Nitrogen (N), % | 0 to 0.1 | |
| 0 |
| Phosphorus (P), % | 0 to 0.045 | |
| 0 to 0.1 |
| Silicon (Si), % | 0 to 0.75 | |
| 0 to 0.010 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.1 |
| Tin (Sn), % | 0 | |
| 5.2 to 8.0 |
| Zinc (Zn), % | 0 | |
| 2.0 to 5.0 |