AISI 304L Stainless Steel vs. SAE-AISI 1117 Steel

Both AISI 304L stainless steel and SAE-AISI 1117 steel are iron alloys. They have 71% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is AISI 304L stainless steel and the bottom bar is SAE-AISI 1117 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 160 to 350
140 to 150
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 6.7 to 46
17 to 26
Fatigue Strength, MPa 170 to 430
190 to 300
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
73
Shear Strength, MPa 370 to 680
320 to 330
Tensile Strength: Ultimate (UTS), MPa 540 to 1160
490 to 540
Tensile Strength: Yield (Proof), MPa 190 to 870
260 to 460

Thermal Properties

Latent Heat of Fusion, J/g 290
250
Maximum Temperature: Mechanical, °C 540
400
Melting Completion (Liquidus), °C 1450
1460
Melting Onset (Solidus), °C 1400
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 16
52
Thermal Expansion, µm/m-K 17
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 2.7
8.1

Otherwise Unclassified Properties

Base Metal Price, % relative 16
1.8
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 3.1
1.4
Embodied Energy, MJ/kg 44
18
Embodied Water, L/kg 150
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 71 to 240
86 to 110
Resilience: Unit (Modulus of Resilience), kJ/m3 92 to 1900
180 to 550
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 19 to 41
17 to 19
Strength to Weight: Bending, points 19 to 31
18 to 19
Thermal Diffusivity, mm2/s 4.2
14
Thermal Shock Resistance, points 12 to 25
15 to 17

Alloy Composition

Carbon (C), % 0 to 0.030
0.14 to 0.2
Chromium (Cr), % 18 to 20
0
Iron (Fe), % 65 to 74
98.3 to 98.8
Manganese (Mn), % 0 to 2.0
1.0 to 1.3
Nickel (Ni), % 8.0 to 12
0
Nitrogen (N), % 0 to 0.1
0
Phosphorus (P), % 0 to 0.045
0 to 0.040
Silicon (Si), % 0 to 0.75
0
Sulfur (S), % 0 to 0.030
0.080 to 0.13

Comparable Variants