AISI 310 Stainless Steel vs. EN 1.7221 Steel

Both AISI 310 stainless steel and EN 1.7221 steel are iron alloys. They have 55% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is AISI 310 stainless steel and the bottom bar is EN 1.7221 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180 to 220
200 to 230
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 34 to 45
11 to 17
Fatigue Strength, MPa 240 to 280
290 to 390
Poisson's Ratio 0.27
0.29
Shear Modulus, GPa 78
73
Tensile Strength: Ultimate (UTS), MPa 600 to 710
650 to 780
Tensile Strength: Yield (Proof), MPa 260 to 350
430 to 630

Thermal Properties

Latent Heat of Fusion, J/g 310
250
Maximum Temperature: Mechanical, °C 1040
420
Melting Completion (Liquidus), °C 1450
1460
Melting Onset (Solidus), °C 1400
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 15
44
Thermal Expansion, µm/m-K 15
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
8.4

Otherwise Unclassified Properties

Base Metal Price, % relative 25
2.4
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 4.3
1.5
Embodied Energy, MJ/kg 61
20
Embodied Water, L/kg 190
51

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 200 to 220
83 to 98
Resilience: Unit (Modulus of Resilience), kJ/m3 170 to 310
490 to 1050
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 21 to 25
23 to 27
Strength to Weight: Bending, points 20 to 22
21 to 24
Thermal Diffusivity, mm2/s 3.9
12
Thermal Shock Resistance, points 14 to 17
19 to 23

Alloy Composition

Carbon (C), % 0 to 0.25
0.22 to 0.29
Chromium (Cr), % 24 to 26
0.8 to 1.2
Iron (Fe), % 48.2 to 57
96.8 to 98.3
Manganese (Mn), % 0 to 2.0
0.5 to 0.8
Molybdenum (Mo), % 0
0.15 to 0.3
Nickel (Ni), % 19 to 22
0
Phosphorus (P), % 0 to 0.045
0 to 0.025
Silicon (Si), % 0 to 1.5
0 to 0.6
Sulfur (S), % 0 to 0.030
0 to 0.030

Comparable Variants