AISI 310 Stainless Steel vs. EN 1.7362 Steel

Both AISI 310 stainless steel and EN 1.7362 steel are iron alloys. They have 59% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is AISI 310 stainless steel and the bottom bar is EN 1.7362 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180 to 220
150 to 180
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 34 to 45
21 to 22
Fatigue Strength, MPa 240 to 280
140 to 250
Poisson's Ratio 0.27
0.29
Shear Modulus, GPa 78
74
Shear Strength, MPa 420 to 470
320 to 370
Tensile Strength: Ultimate (UTS), MPa 600 to 710
510 to 600
Tensile Strength: Yield (Proof), MPa 260 to 350
200 to 360

Thermal Properties

Latent Heat of Fusion, J/g 310
260
Maximum Temperature: Mechanical, °C 1040
510
Melting Completion (Liquidus), °C 1450
1460
Melting Onset (Solidus), °C 1400
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 15
40
Thermal Expansion, µm/m-K 15
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
8.1
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
9.4

Otherwise Unclassified Properties

Base Metal Price, % relative 25
4.5
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 4.3
1.8
Embodied Energy, MJ/kg 61
23
Embodied Water, L/kg 190
69

Common Calculations

PREN (Pitting Resistance) 25
6.9
Resilience: Ultimate (Unit Rupture Work), MJ/m3 200 to 220
90 to 110
Resilience: Unit (Modulus of Resilience), kJ/m3 170 to 310
100 to 340
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 21 to 25
18 to 21
Strength to Weight: Bending, points 20 to 22
18 to 20
Thermal Diffusivity, mm2/s 3.9
11
Thermal Shock Resistance, points 14 to 17
14 to 17

Alloy Composition

Carbon (C), % 0 to 0.25
0.1 to 0.15
Chromium (Cr), % 24 to 26
4.0 to 6.0
Copper (Cu), % 0
0 to 0.3
Iron (Fe), % 48.2 to 57
91.5 to 95.2
Manganese (Mn), % 0 to 2.0
0.3 to 0.6
Molybdenum (Mo), % 0
0.45 to 0.65
Nickel (Ni), % 19 to 22
0 to 0.3
Nitrogen (N), % 0
0 to 0.012
Phosphorus (P), % 0 to 0.045
0 to 0.020
Silicon (Si), % 0 to 1.5
0 to 0.5
Sulfur (S), % 0 to 0.030
0 to 0.0050